1066 65MN T10A Spring Steel
Dimensi: dia. 0.1 mm
Pengukur Kabel: 0,1mm 20mm
Tempat Asal: Zhejiang Cina (daratan)Negara | Cina | Jerman | Inggris | AS |
Standar | GB | / | BS | AISI/SAE/ASTM |
Kelas | 65-n | / | 080A67 | 1066 |
Kelas | C | Si | MN | P | S | CR | NI |
65-n | 0.62-0.70 | 0.17-0.37 | 0.90-1.20 | 0.035 Maks. | 0.035 Maks. | 0.25 | 0.25 |
1066 | 0.6-0.71 | / | 0.85-1.15 | 0.04 | 0.05 | / | / |
Sifat mekanis terutama mencakup kekuatan tensil, kekuatan yield, pemanjangan, area atau reduksi, kekerasan, Nilai dampak, inklusi tidak logam dll. perlakuan panas berbeda, sifat mekanis akan berbeda, seperti Normalized, diperkeras, QT. Jika Anda ingin mengetahui properti-sifat tersebut, silakan hubungi salesman.
5: Overview baja 65Mn
Ukuran | Bundar | Dia 6-1200 mm |
Pelat/datar/Blok | Ketebalan 6mm-500mm |
|
Lebar 20 mm-1000mm |
||
Perlakuan panas | Dinormalkan ; Anneap ; mengalami quefed ; Tempered | |
Kondisi permukaan | Hitam; dikupas; dibuat dari mesin; ditentukan oleh: Berputar; dikikis | |
Kondisi pengiriman | Ditempa; rol panas; ditarik dingin | |
Uji | Kekuatan tensil, kekuatan yield, pemanjangan, area reduksi, nilai benturan, Kekerasan, ukuran biji, tes ultrasonik, inspeksi di AS, tes partikel magnetik, dll.. | |
Ketentuan pembayaran | T/T;L/C;/gram uang/ Paypal | |
Ketentuan perdagangan | FOB; CIF; C&F; DLL.. | |
Waktu pengiriman | 30-45 hari | |
Aplikasi | Baja karbon tinggi 65Mn sebagian besar digunakan pada pembentukan berbagai mata air datar bagian kecil, pegas bundar, jam kerja, dll. Selain itu juga dapat digunakan untuk memproduksi cincin pegas, pegas katup, penyerap kejut, ulag kopling dan pegas rem, mengatur kecepatan pegas, beban pegas, mesin umum pada ronde kondisi berputar, pegas spiral persegi atau kabel untuk menarik pegas mekanis kecil. |
6. Terkait perlakuan panas
Annealing
Pada awalnya, pemanas hingga 730 derajat celcius dan berikan waktu yang cukup, biarkan baja dipanaskan seluruhnya, kemudian dingin perlahan dalam tungku. Lalu 65Mn tool steel akan mendapatkan maks 250 HB (kekerasan Brinell).
Hardening
Pada mulanya, baja 65 Mn harus dipanaskan sama-sama hingga 830-860 1526 C (1580- o F) hingga dipanaskan seluruhnya. Setelah sekitar 30 mnt per 25 mm bagian memerintah akan disediakan dan kemudian baja harus segera mengalami quenching dalam oli.
Pengerasan
Baja 65 Mn dilakukan pada 540 o C, rendam dengan baik pada temperatur yang dipilih dan rendam dalam sekurangnya satu jam per 25mm ketebalan total. Nilai kekerasan pada suhu berbeda setelah tempering.
7: Kondisi pengiriman
Untuk batang rol tempa yang panas, biasanya kondisi pengiriman ditempa atau digulung, tidak diudara/QT, dengan permukaan kasar diputar/Hitam.Untuk pelat rol yang panas, biasanya kondisi penyaluran digilirkan, tidak disbanding/QT, permukaan hitam.
GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-NR) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
Baja Work Tool dingin | ||||
1.2080/X210C12 | D3 | |||
C5M1V | SKD12 | 1.2363/X100CMoV5 | A2/T30102 | BA2 |
C12MV | 1.2601 | D5 | ||
Cr12M1V1 | SKD11 | 1.2379/X153Crm12 | D2 | |
X210CW12 | SKD2 | 1.2436 | D6 | |
9Crawn | SKS3 | 1.2510/100MnCrW4 | O1 | |
9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
5Crsen Mo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
Baja Work Tool panas | ||||
1.2355/50CrMoV13-15 | S7/T41907 | |||
5CrNiMV | 1.2714 | 6F3 | ||
5Crsen Ni4Mo | 1.2767 | 6F7 | ||
SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
4Crac5MoV | SKD6 | 1.2343/X37CMoV5-1 | H11/T20811 | BH11 |
4Crac5 MoSiV1 | SKD61 | 1.2344/X40CMoV5-1 | H13 | |
SKD62 | 1.2605/X35CWMoV5 | H12/T20812 | BH12 | |
3Cr2W8V | SKD5 | 1.2581 | H21 | |
Baja mold plastik | ||||
3Cr2Mo | 1.2311 | P20 | ||
NAK80 | 1.2312 | P20+S / P21 | ||
3Cr2MnNiMong | 1.2738 | P20+Ni / 718 | ||
4C13 | SUS420J2 | 1.2083 | 415 | |
3C17+S | SUS420F | 1.2085 | ||
3Cr17Mo | SUS420J | 1.2316 | ||
Baja Teknik | ||||
GB GB/T 699 |
JIS JIS G4051 |
DIN (W-NR) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
1018 | EN2C | |||
20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
S35C | C35 | 1035 | ||
1040 | EN8/080M40 | |||
45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
50 | S50C | 1050 | ||
S55C | 1055 | EN9/070M55 | ||
Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-NR) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
40Cr | SCr440 | 41CR4(1.7035) | 5140 | |
SCM420 | 18CMo4/1.7243 | 4118 | ||
30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
42CrMo | SCM440 | 42cr4/1.7225 | 4140 | EN19/709M40 |
4145 | ||||
4330 | ||||
40CronNikMA | SNCM 439/SNCM8 | 36CronMo4/1.6511 | 4340 | EN24/817M40 |
40NiMCris10-5/1.6745 | EN26 | |||
34CronMo6 / 1.6582 | 4337 | |||
30Cronmo16-6/1.6747 | EN30B/835M30 | |||
32CrMo12/1.7361 | EN40B/722M24 | |||
SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
15Krtidak 6/1.5919 | 3115 | |||
16NiC4/1.5714 | EN351/635M15 | |||
4615/4617 | EN34/665M17 | |||
14tiada 1.5752 | 3310/3415 | EN36/655M13 | ||
15Kritmo16-5/1.6723 | EN39/835M15 | |||
18Cran787-6 (1.6587) | 4815 | |||
SNCM220 | 1.6523/21NiCMo2 | 8620 | 805M20 | |
20CronNiM5 | EN353 | |||
GCr15 | 52100/1.3505 | EN31/535A99 | ||
Baja Antikarat | ||||
SUS440C | X105CMo17/1.4125 | S44004/440C | ||
Keausan-menolak Baja | ||||
GB | JIS | DIN (W-NR) | AISI/ASTM | SSAB |
HB400 | ||||
NHOTEL | HB500 | |||
Baja pegas | ||||
GB | JIS | DIN (W-NR) | AISI/ASTM | SSAB |
65MN | 1066 | |||
60Si2Mn | SUP6 | 60Si7 | 9260 | |
60Si2MnA | SUP7 | 60Si7 | 9260 | |
55CCraMA | SUP9 | 55C3 | 5155 | |
60CnA | SUP9A | 5160 | ||
50CVA | SUP10 | 51CrV4 | 6150 | |
Baja Kecepatan Tinggi | ||||
GB | JIS JIS G4403 |
DIN (W-NR) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
SKH51 | 1.3343 | M2 | ||
SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
SKH2 | HS18-0-1/1.3355 | T1 | ||
SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
Semua jenis komponen penempaan sesuai Gambar |
Ukuran | Bundar | Dia 8-1200 mm |
Pelat/datar/Blok | Ketebalan 10 mm-800mm |
|
Lebar 20 mm-2000mm |
||
Perlakuan panas | Dinormalkan ; Anneap ; mengalami quefed ; Tempered | |
Kondisi permukaan | Hitam; dikupas; dibuat dari mesin; ditentukan oleh: Berputar; dikikis | |
Kondisi pengiriman | Ditempa; rol panas; ditarik dingin | |
Uji | Kekuatan tensil, kekuatan yield, pemanjangan, area reduksi, nilai benturan, Kekerasan, ukuran biji, tes ultrasonik, inspeksi di AS, tes partikel magnetik, dll.. | |
Ketentuan pembayaran | T/T;L/C;/gram uang/ Paypal | |
Ketentuan perdagangan | FOB; CIF; C&F; DLL.. | |
Waktu pengiriman | 30-45 hari |