Tipe: | Coil Baja tahan karat |
---|---|
Standar: | ASTM, AISI, GB, JIS, DIN, ID |
Kelas: | Seri 300 |
Sertifikasi: | ISO, IBR, AISI, ASTM, GB, ID |
Bentuk: | Bundar |
Teknik: | Hot Rolling/Cold Rolling |
Pemasok dengan izin usaha terverifikasi
Lebar | Ketebalan | Diameter dalam | Kelas Baja | Permukaan Selesai |
610-1524 mm | 0.3 mm. 3.0 mm | 610 atau 508 +0/-5 mm | 201, 202, 204 Cu3, 301, 304, 304L, 310S, 316L, 321, 409L, 410S, 420J2, 430, 439, 441, 444, 445 | BA, 2B, 2D, 4K, 6K, 8 K, NO.4, HL, SB, TIMBUL |
Ketebalan (mm) | 630≤Lebar<1000 (mm) | 1000≤Lebar<1250 (mm) | 1250≤Lebar<1550 (mm) |
0.25 ≤ T < 0.40 | ±0.030 | ±0.035 | - |
0.40 ≤ T < 0.60 | ±0.035 | ±0.035 | - |
0.60 ≤ T < 0.80 | ±0.040 | ±0.040 | - |
0.80 ≤ T < 1.00 | ±0.040 | ±0.050 | ±0.050 |
1.00 ≤ T < 1.25 | ±0.050 | ±0.055 | ±0.060 |
1.25 ≤ T < 1.60 | ±0.055 | ±0.060 | ±0.060 |
1.60 ≤ T < 2.00 | ±0.065 | ±0.070 | ±0.080 |
Kelas baja | NI Max. | CR Max. | C Maks. | Si Maks. |
301 | 6.0-8.0 | 16.0-18.0 | 0.15 | 1.0 |
304 | 8.0-10.5 | 18.0-20.0 | 0.08 | 1.0 |
304L | 9.0-13.0 | 18.0-20.0 | 0.03 | 1.0 |
310S. | 19.0-22.0 | 24.0-26.0 | 0.08 | 1.5 |
316L | 12.0-15.0 | 16.0-8.0 | 0.03 | 1.0 |
321 | 9.0-13.0 | 17.0-19.0 | 0.08 | 1.0 |
430 | 0.6 | 16.0-18.0 | 0.12 | 0.75 |
Kelas Baja | Kekuatan tensil N/ mm2 Min. |
Menghasilkan kekuatan N/ mm2 Min. |
Naskh (Naskh) Min. |
Kekerasan HRB Maks. |
301 | 520 | 205 | 40 | 95 |
304 | 520 | 205 | 40 | 90 |
304L | 480 | 175 | 40 | 90 |
310S. | 520 | 205 | 40 | 90 |
316L | 480 | 175 | 40 | 90 |
321 | 520 | 205 | 40 | 90 |
430 | 420 | 205 | 22 | 88 |