Type: | Sheet |
---|---|
Standard: | AISI, ASTM, DIN, JIS, GB, BS |
Composition: | Check Detailed Description |
Technique: | Hot Rolled |
Shape: | Flat |
Surface Treatment: | Black, Machined |
Pemasok dengan izin usaha terverifikasi
Baja Campuran suku Cadang dengan Baja Khusus DIN datar 1.2358 Lembar pelat Baja Alat Baja yang sangat baik Blok ROUND Bar
Komposisi kimia (%)
C | SL | MN | P | S | CR | MO | V |
0.55 | 0.20 | 0.70 | ≤ | ≤ | 4.20 | 0.30 | 0.15 |
0.65 | 0.40 | 0.90 | 0.030 | 0.030 | 4.80 | 0.70 | 0.25 |
Dimensi
Bentuk | Tebal (mm) | Lebar (mm) | |||
Rata | 6-200 | 20-1000 | |||
Blok | 150-500 | 200-1000 |
Kondisi pengiriman
EAF+LF+VD+(ESR), Hot olled atau tempa, tanpa pemesinan atau hasil pemesinan, UT 100% lulus
Kami menawarkan kondisi AnneN dan Q+T.
Anneem: Kekerasan≤240HB
Q+T: KEKERASAN 30-34 HRC
Karakteristik
Ianya sejenis baja work tool dengan mata beku sedang yang biasanya disuplai keras, keras
kapasitas pengerasan melalui kekerasan dan ketangguhan, kemampuan las yang baik, kemampuan permukaan yang luar biasa.
Aplikasi
Untuk memasukkan sisipan pemotong untuk alat tersegmentasi, alat sching, pisau geser, geraham plastik, alat pemotong.
Perlakuan panas
Annealing
820 hingga 860 derajat C
Pendinginan yang dikendalikan secara lambat di tungku dengan kecepatan 10 hingga 20 600/jam hingga suhu derajat, lebih sejuk di udara.
Kekerasan setelah annealing: Maks. 240 HB.
Selongsong penghilang stres
600 hingga 650 derajat C
Pendinginan lambat di tungku; untuk melepaskan tegangan yang telah disetel dari pengerjaan dengan mesin ekstensif atau bentuk tidak kompleks.
Setelah melalui pemanasan, pegang atmosfer netral selama 1 hingga 2 jam.
Hardening
950 hingga 980 derajat C
Bentuk/udara yang rumit, bentuk/hembusan udara sederhana, minyak, garam mandi mulai 220 hingga 250 o C atau 500 hingga 550 derajat. Waktu Holding
setelah penyetaraan suhu: 15 hingga 30 menit.
Kekerasan bisa diperoleh: 63 - 65 HRC.
Pengerasan
Pemanasan yang lambat akan mengeraskan udara segera setelah hardening/waktu dalam tungku
1jam untuk masing-masing ketebalan bagian kerja 20 mm, tetapi setidaknya 2 jam/pendinginan di udara.
Kami menawarkan berbagai produk baja dalam berbagai dimensi dan pelaksanaan, menurut spesifikasi internasional umum atau kustomisasi.
Tersedia pengerjaan dengan mesin dan panas.
Kami juga menyarankan Anda memilih materi yang tepat.
Bentuk tersedia
Bar bundar yang solid
Batang datar
Bar persegi
Bilah segi enam
Blok
Pelat
Lembar
Batang kabel
Strip
|
AISI |
DIN |
JIS |
Saham |
Aplikasi |
Baja Work Tool panas |
H11 |
1.2343 |
SKD6 |
√ |
Cetakan die Casies, tonjolan, Cetakan Hammer, |
H13 |
1.2344 |
SKD61 |
√ |
||
H10 |
1.2365 |
SKD7 |
|
||
-- |
1.2367 |
-- |
|
||
L6 |
1.2714 / 1.2713 |
SKT4 |
√ |
||
H12 |
1.2606 |
SKD62 |
|
||
H21 |
1.2581 |
SKD5 |
√ |
||
Baja Work Tool dingin |
D3 |
1.2080 |
|
√ |
Alat Pemotongan, Alat Bantu, arah Shear Blader, Reamers, Ulir Geli, Kaliper, Soket, dll. |
-- |
1.2601 |
SKD11 |
√ |
||
D2 |
1.2379 |
SKD11 |
√ |
||
-- |
1.2379 MOD |
DC53 (Daido) |
√ |
||
D6 |
1.2436 |
-- |
|
||
O1 |
1.2510 |
SKS3 |
√ |
||
O2 |
1.2842 |
-- |
|
||
A2 |
1.2363 |
SKD12 |
|
||
S1 |
1.2550 |
-- |
|
||
S7 |
1.2357 |
-- |
|
||
-- |
1.2767 |
SKT6 |
|
||
L2 |
1.2210 |
-- |
|
||
Plastik |
P20 |
1.2311 |
-- |
√ |
Basis mold, Core & cavity, Bumper mold dll. |
P20+Ni |
1.2738 |
-- |
√ |
||
P20+S |
1.2312 |
-- |
√ |
||
-- |
1.2316 |
-- |
|
||
420 |
1.2083 |
SUS420J2 |
√ |
||
-- |
-- |
NAK80 (Daido) |
√ |
||
Baja Campuran |
4120 |
25CrMo4 / 1.7218 |
SCM420 |
|
Poros, roda gigi, pengebor, rantai, baut, Mur, pin, Sud, tombol, Bites, Crankshaft, Connecting Rod, disertakan, kopling Sambungan, dll. |
4135 |
34CrMo4 / 1.7220 |
SCM435 |
|
||
4130 |
34CrMo4 / 1.7220 |
SCM430 |
√ |
||
4140 |
42CrDepar4 / 1.7225 |
SCM440 |
√ |
||
4142 |
41CMo4 / 1.7223 |
SCM440 |
|
||
4145H |
-- |
-- |
|
||
330V |
-- |
-- |
|
||
4340 |
34CronMo6 / 1.6582 |
|
|
||
5115 |
16MnCr5 / 16MnCrS5 / 1.7131 |
|
|
||
5120 |
20MnCr5 / 20MnCrS5 / 1.7147 |
SMnC420H |
|
||
5140 |
41CR4 / 41crS4 / 1.7035 |
SCr440 |
√ |
||
8620 |
21NiCMo2 / 1.6523 |
SNCM220 |
|
||
8640 |
40NiCM2-2 / 1.6546 |
|
|
||
-- |
18Kren-6 / 17CronnM6 / 1.6587 |
-- |
|
||
9840 |
36CronMo4 / 1.6511 |
-- |
|
||
E71400 |
41Klungkir7-10 / 1.8509 |
SACM1 |
|
||
-- |
34Kren / 1.8550 |
-- |
|
||
Bearing Steel |
E52100 |
100Cr6 / 1.3505 |
SUJ2 |
√ |
Bearing, poros |
-- |
100CrMn6 / 1.3520 |
-- |
|
||
-- |
100CrDepan7-3 / 1.3536 |
-- |
|
||
Baja pegas |
5155 |
55C3 / 1.7176 |
SUP9 |
|
Pegas |
6150 |
51CrV4 / 1.8159 |
SUP10 |
|
||
9261 |
60CrSi7 / 1.7108 |
-- |
|
||
Baja Karbon |
1010 |
C10 / C10E / 1.1121 |
S10C |
|
Poros, Rantai, baut, mur, pin, Suld, Kunci, Bites, Finding, Fupling, dll. |
1020 |
C22 / 1.0402 |
S20C |
√ |
||
1040 |
C4040 / C40E / 1.1186 |
S40C |
√ |
||
1045 |
CKM45 / C45E / 1.1191 |
S45C |
√ |
||
1050 |
C50 / C50E / 1.1206 |
S50C |
√ |
||
1055 |
C55E / 1.1203 |
S55C |
|
||
1064 |
C60 / C60E / 1.1221 |
S58C |
|
||
Baja Alat Kecepatan Tinggi |
M2 |
1.3343 |
SKH51 |
√ |
Reer, |
M7 |
1.3348 |
-- |
|
||
M42 |
1.3247 |
SKH59 |
√ |
||
M35 |
1.3243 |
SKH55 |
√ |
||
T1 |
1.3355 |
SKH2 |
|
||
T15 |
1.3202 |
-- |
|
||
T42 |
1.3207 |
SKH57 |
|
Catatan:
1). √ bererti kita mempunyai stoc
2). Kondisi pengiriman:
PELEBURAN: EAF+LF+VD (+ESR)
Pembuatan: Rol panas, dingin digulung, ditempa, dan dingin terisap
Perlakuan panas: Tidak diobati, Annealing, N+T, Q+T
Permukaan: Hitam, dikupas, berputar, diatur, diatur, dan diatur, Dipoles
Pemasok dengan izin usaha terverifikasi