Type: | Steel Plate |
---|---|
Standard: | ASTM, AISI, GB, JIS, DIN, BS |
Certification: | ISO |
Surface Treatment: | Black, Machined |
Technique: | Hot Rolled |
Application: | Mold & Dies |
Pemasok dengan izin usaha terverifikasi
A isi 420 Baja mold plastik
Kesetaraan
AlSl / SAE | DIN / W.NR | JIS | GB | ||||||||
420 | 1.2083 | SUS420J2 | 4C13 | ||||||||
Komposisi kimia (%)
Kelas Baja | C | Si | MN | P | S | CR | |||||||
1.2083 | 0.36 | ≤ | ≤ | ≤ | ≤ | 12.50 | |||||||
0.42 | 1.00 | 1.00 | 0.030 | 0.030 | 14.50 | ||||||||
420 | ≤ | ≤ | ≤ | ≤ | ≤ | 12.00 | |||||||
0.15 | 1.00 | 1.00 | 0.030 | 0.030 | 14.00 | ||||||||
4C13 | 0.36 | ≤ | ≤ | ≤ | ≤ | 12.00 | |||||||
0.45 | 0.60 | 0.80 | 0.030 | 0.030 | 14.00 |
Dimensi
Bentuk | Tebal / Dia.(mm) | Lebar (mm) | ||||||
Rata | 6-200 | 20-910 | ||||||
Pelat | 6-120 | 1000-2300 | ||||||
Blok | 150-600 | 200-1500 |
Kondisi pengiriman
EAF+LF+VD+(ESR), ditempa, tidak diproses mesin atau diproses mesin, UT 100% lulus
Kami menawarkan dua syarat
Anneem: Kekerasan≤235HB
Q+T: Kekerasan 33-38HRC atau seperti disesuaikan
Karakteristik
Baja anti karat dari tempat MarcTeng, dengan daya yang baik dan ketahanan korosi yang sangat baik, daya ishabilitas, serta kekuatan tinggi dan ketahanan aus setelah perlakuan panas.
Aplikasi
Alat ini juga digunakan secara luas untuk membuat cetakan plastik dan cetakan plastik transparan yang memerlukan beban tinggi, ketahanan aus, dan bekerja di bawah aksi medium yang berkarat.
Teknik Tempa
Perlakuan panas
Suhu panas | Mulai suhu Tempa | Suhu Tempa | Metode Pendinginan |
Panas perlahan hingga 800 derajat, lalu cepat panas ke suhu penempaan akhir | 1160-1200 | >=81 ATAU 50 DERAJAT | Pendinginan abu dingin dan pasir, dengan annealing tepat waktu |
Annealing
840 hingga 870 derajat C
Pendinginan yang dikendalikan secara lambat di tungku dengan kecepatan 10 hingga 20 600/jam hingga suhu derajat, lebih sejuk di udara. Kekerasan setelah annealing: Maks. 229 HB.
Selongsong penghilang stres
Sekitar 650 DERAJAT C
Pendinginan lambat di tungku; untuk melepaskan tegangan yang telah disetel dari pengerjaan dengan mesin ekstensif atau dalam bentuk kompleks. Setelah melalui pemanasan, pegang atmosfer netral selama 1 - 2 jam.
Hardening
1000 hingga 1050 C / Oli, udara
Menahan waktu setelah penyetaraan suhu: 15 hingga 30 menit.
Kesadahan dapat diperoleh: 53-56 HRC
Pengerasan
100 hingga 200 o C (212 hingga 392 o F)
Pemanasan yang lambat akan mengeraskan segera setelah hardening / waktu dalam tungku
1 jam untuk masing-masing ketebalan bagian kerja 20 mm, tetapi setidaknya 2 jam/pendinginan di udara.
Untuk angka kekerasan rata-rata yang akan diperoleh, baca bagan pengerasan.
Apa yang dapat kami tawarkan?
Kami menawarkan berbagai produk baja dalam berbagai dimensi dan pelaksanaan, menurut spesifikasi internasional umum atau kustomisasi.
Tersedia pengerjaan dengan mesin dan panas.
Kami juga menyarankan Anda memilih materi yang tepat.
Bentuk tersedia
Bar bundar yang solid
Batang datar
Bar persegi
Bilah segi enam
Blok
Pelat
Lembar
Batang kabel
Strip
|
AISI |
DIN |
JIS |
Saham |
Aplikasi |
Baja Work Tool panas |
H11 |
1.2343 |
SKD6 |
√ |
Cetakan die Casies, tonjolan, Cetakan Hammer, |
H13 |
1.2344 |
SKD61 |
√ |
||
H10 |
1.2365 |
SKD7 |
|
||
-- |
1.2367 |
-- |
|
||
L6 |
1.2714 / 1.2713 |
SKT4 |
√ |
||
H12 |
1.2606 |
SKD62 |
|
||
H21 |
1.2581 |
SKD5 |
√ |
||
Baja Work Tool dingin |
D3 |
1.2080 |
|
√ |
Alat Pemotongan, Alat Bantu, arah Shear Blader, Reamers, Ulir Geli, Kaliper, Soket, dll. |
-- |
1.2601 |
SKD11 |
√ |
||
D2 |
1.2379 |
SKD11 |
√ |
||
-- |
1.2379 MOD |
DC53 (Daido) |
√ |
||
D6 |
1.2436 |
-- |
|
||
O1 |
1.2510 |
SKS3 |
√ |
||
O2 |
1.2842 |
-- |
|
||
A2 |
1.2363 |
SKD12 |
|
||
S1 |
1.2550 |
-- |
|
||
S7 |
1.2357 |
-- |
|
||
-- |
1.2767 |
SKT6 |
|
||
L2 |
1.2210 |
-- |
|
||
Plastik |
P20 |
1.2311 |
-- |
√ |
Basis mold, Core & cavity, Bumper mold dll. |
P20+Ni |
1.2738 |
-- |
√ |
||
P20+S |
1.2312 |
-- |
√ |
||
-- |
1.2316 |
-- |
|
||
420 |
1.2083 |
SUS420J2 |
√ |
||
-- |
-- |
NAK80 (Daido) |
√ |
||
Baja Campuran |
4120 |
25CrMo4 / 1.7218 |
SCM420 |
|
Poros, roda gigi, pengebor, rantai, baut, Mur, pin, Sud, tombol, Bites, Crankshaft, Connecting Rod, disertakan, kopling Sambungan, dll. |
4135 |
34CrMo4 / 1.7220 |
SCM435 |
|
||
4130 |
34CrMo4 / 1.7220 |
SCM430 |
√ |
||
4140 |
42CrDepar4 / 1.7225 |
SCM440 |
√ |
||
4142 |
41CMo4 / 1.7223 |
SCM440 |
|
||
4145H |
-- |
-- |
|
||
330V |
-- |
-- |
|
||
4340 |
34CronMo6 / 1.6582 |
|
|
||
5115 |
16MnCr5 / 16MnCrS5 / 1.7131 |
|
|
||
5120 |
20MnCr5 / 20MnCrS5 / 1.7147 |
SMnC420H |
|
||
5140 |
41CR4 / 41crS4 / 1.7035 |
SCr440 |
√ |
||
8620 |
21NiCMo2 / 1.6523 |
SNCM220 |
|
||
8640 |
40NiCM2-2 / 1.6546 |
|
|
||
-- |
18Kren-6 / 17CronnM6 / 1.6587 |
-- |
|
||
9840 |
36CronMo4 / 1.6511 |
-- |
|
||
E71400 |
41Klungkir7-10 / 1.8509 |
SACM1 |
|
||
-- |
34Kren / 1.8550 |
-- |
|
||
Bearing Steel |
E52100 |
100Cr6 / 1.3505 |
SUJ2 |
√ |
Bearing, poros |
-- |
100CrMn6 / 1.3520 |
-- |
|
||
-- |
100CrDepan7-3 / 1.3536 |
-- |
|
||
Baja pegas |
5155 |
55C3 / 1.7176 |
SUP9 |
|
Pegas |
6150 |
51CrV4 / 1.8159 |
SUP10 |
|
||
9261 |
60CrSi7 / 1.7108 |
-- |
|
||
Baja Karbon |
1010 |
C10 / C10E / 1.1121 |
S10C |
|
Poros, Rantai, baut, mur, pin, Suld, Kunci, Bites, Finding, Fupling, dll. |
1020 |
C22 / 1.0402 |
S20C |
√ |
||
1040 |
C4040 / C40E / 1.1186 |
S40C |
√ |
||
1045 |
CKM45 / C45E / 1.1191 |
S45C |
√ |
||
1050 |
C50 / C50E / 1.1206 |
S50C |
√ |
||
1055 |
C55E / 1.1203 |
S55C |
|
||
1064 |
C60 / C60E / 1.1221 |
S58C |
|
||
Baja Alat Kecepatan Tinggi |
M2 |
1.3343 |
SKH51 |
√ |
Reer, |
M7 |
1.3348 |
-- |
|
||
M42 |
1.3247 |
SKH59 |
√ |
||
M35 |
1.3243 |
SKH55 |
√ |
||
T1 |
1.3355 |
SKH2 |
|
||
T15 |
1.3202 |
-- |
|
||
T42 |
1.3207 |
SKH57 |
|
Annealing
840 hingga 870 derajat C
Pendinginan yang dikendalikan secara lambat di tungku dengan kecepatan 10 hingga 20 600/jam hingga suhu derajat, lebih sejuk di udara. Kekerasan setelah annealing: Maks. 229 HB.
Selongsong penghilang stres
Sekitar 650 DERAJAT C
Pendinginan lambat di tungku; untuk melepaskan tegangan yang telah disetel dari pengerjaan dengan mesin ekstensif atau dalam bentuk kompleks. Setelah melalui pemanasan, pegang atmosfer netral selama 1 - 2 jam.
Hardening
1000 hingga 1050 C / Oli, udara
Menahan waktu setelah penyetaraan suhu: 15 hingga 30 menit.
Kesadahan dapat diperoleh: 53-56 HRC
Pengerasan
100 hingga 200 o C (212 hingga 392 o F)
Pemanasan yang lambat akan mengeraskan segera setelah hardening / waktu dalam tungku
1 jam untuk masing-masing ketebalan bagian kerja 20 mm, tetapi setidaknya 2 jam/pendinginan di udara.
Untuk angka kekerasan rata-rata yang akan diperoleh, baca bagan pengerasan.
Apa yang dapat kami tawarkan?
Kami menawarkan berbagai produk baja dalam berbagai dimensi dan pelaksanaan, menurut spesifikasi internasional umum atau kustomisasi.
Tersedia pengerjaan dengan mesin dan panas.
Kami juga menyarankan Anda memilih materi yang tepat.
Bentuk tersedia
Bar bundar yang solid
Batang datar
Bar persegi
Bilah segi enam
Blok
Pelat
Lembar
Batang kabel
Strip
Catatan:
1). √ bererti kita mempunyai stoc.
2). Kondisi pengiriman:
PELEBURAN: EAF+LF+VD (+ESR).
Pembuatan: Rol panas, dingin digulung, ditempa, dan dingin terisap.
Perlakuan panas: Tidak diobati, Annealing, N+T, Q+T.
Permukaan: Hitam, dikupas, berputar, diatur, diatur, dan diatur, Dipoles.
Pemasok dengan izin usaha terverifikasi