Standard: | JIS, GB, DIN, BS, ASTM, AISI |
---|---|
Application: | Loader, Construction Machinery, Metallurgical Machinery, Mining Machine |
Material: | Steel |
Type: | Wear Resistant Plate |
kekerasan utama: | 400hb 500hb |
pelat keausan anti aus di peru: | pelat perlindungan di peru |
Pemasok dengan izin usaha terverifikasi
Komposisi kimia | pelat baja | C | Si | MN | P | S | CR | NI |
Thicess | % | % | % | % | % | % | % | |
2 mm | 0.11-0.20 | 0.38-0.55 | 1.20-1.55 | 0.005-0.020 | 0.005-0.010 | 0.01-0.60 | 0.004-0.04 | |
Kekerasan | 370-430HB | |||||||
Sifat Mekanis | nilai khusus pelat baja ketebalan 10 mm | Kekuatan yang menusuk | Kekuatan tensil | Naskh (Naskh) | ||||
Re | RM | A5 | ||||||
MPa | MPa | % | ||||||
>1050 | >1250 | 12 | ||||||
Kekerasan benturan | nilai khusus pelat baja ketebalan 10 mm | Uji | Tes benturan | |||||
Suhu | Charpy-V Longitudinal | |||||||
J | ||||||||
-20 | 40 |
Komposisi kimia | pelat baja | C | Si | MN | P | S | CR | NI |
Thicess | % | % | % | % | % | % | % | |
2 mm | 0.20-0.26 | 0.75-0.95 | 1.60-1.80 | 0.015-0.020 | 0.005-0.010 | 0.01-0.60 | 0.001-0.04 | |
Kekerasan | 420-480HB | |||||||
Sifat Mekanis | nilai khusus pelat baja ketebalan 10 mm | Kekuatan yang menusuk | Kekuatan tensil | Naskh (Naskh) | ||||
Re | RM | A5 | ||||||
MPa | MPa | % | ||||||
>1150 | >1300 | 10 | ||||||
Kekerasan benturan | nilai khusus pelat baja ketebalan 10 mm | Uji | Tes benturan | |||||
Suhu | Charpy-V Longitudinal | |||||||
J | ||||||||
-20 | 30 |
Komposisi kimia | pelat baja | C | Si | MN | P | S | CR | NI |
Thicess | % | % | % | % | % | % | % | |
2 mm | 0.25-0.35 | 0.25-1.75 | 0.40-1.60 | 0.015-0.020 | 0.005-0.010 | 0.20-0.80 | 0.001-0.03 | |
Kekerasan | 470-530HB | |||||||
Sifat Mekanis | nilai khusus pelat baja ketebalan 10 mm | Kekuatan yang menusuk | Kekuatan tensil | Naskh (Naskh) | ||||
Re | RM | A5 | ||||||
MPa | MPa | % | ||||||
>1250 | >1500 | 8 | ||||||
Kekerasan benturan | nilai khusus pelat baja ketebalan 10 mm | Uji | Tes benturan | |||||
Suhu | Charpy-V Longitudinal | |||||||
J | ||||||||
-20 | 20 |
Komposisi kimia | pelat baja | C | Si | MN | P | S | CR | NI |
Thicess | % | % | % | % | % | % | % | |
2 mm | 0.30-0.37 | 0.2-0.405 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.30-0.80 | 0.002-0.60 | |
Kekerasan | 520-580HB | |||||||
Sifat Mekanis | nilai khusus pelat baja ketebalan 10 mm | Kekuatan yang menusuk | Kekuatan tensil | Naskh (Naskh) | ||||
Re | RM | A5 | ||||||
MPa | MPa | % | ||||||
>1300 | >1550 | 6 | ||||||
Kekerasan benturan | nilai khusus pelat baja ketebalan 10 mm | Uji | Tes benturan | |||||
Suhu | Charpy-V Longitudinal | |||||||
J | ||||||||
-20 | 12 |
Komposisi kimia | pelat baja | C | Si | MN | P | S | CR | NI |
Thicess | % | % | % | % | % | % | % | |
2 mm | 0.35-0.40 | 0.20-0.80 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.25-1.00 | 0.002-0.60 | |
Kekerasan | 560-620HB | |||||||
Sifat Mekanis | nilai khusus pelat baja ketebalan 10 mm | Kekuatan yang menusuk | Kekuatan tensil | Naskh (Naskh) | ||||
Re | RM | A5 | ||||||
MPa | MPa | % | ||||||
>1450 | >1650 | 5 | ||||||
Kekerasan benturan | nilai khusus pelat baja ketebalan 10 mm | Uji | Tes benturan | |||||
Suhu | Charpy-V Longitudinal | |||||||
J | ||||||||
-20 | 8 |
Komposisi kimia | pelat baja | C | Si | MN | P | S | CR | NI |
Thicess | % | % | % | % | % | % | % | |
2 mm | 0.40-0.50 | 0.20-0.80 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.80-1.50 | 0.002-0.60 | |
Kekerasan | 620-680HB | |||||||
Sifat Mekanis | nilai khusus pelat baja ketebalan 10 mm | Kekuatan yang menusuk | Kekuatan tensil | Naskh (Naskh) | ||||
Re | RM | A5 | ||||||
MPa | MPa | % | ||||||
>1500 | >1750 | 3 | ||||||
Kekerasan benturan | nilai khusus pelat baja ketebalan 10 mm | Uji | Tes benturan | |||||
Suhu | Charpy-V Longitudinal | |||||||
J | ||||||||
-20 | 6 |