Pelat baja yang dipakai MGN400
pelat baja memotong dan membungkuk sesuai dengan gambar klien
pelat baja yang dipotong
Pelat baja keras keras keras keras keras 500
PELAT BAJA AR500 abrasi
Nama |
Kelas |
Ketebalan (mm) |
Lebar (mm) |
Kondisi Suplai |
Layanan kami |
Pelat keras/pelat baja abrasi/pelat baja tahan aus |
// |
6-80 |
1600-3500 |
Q,Q+T,TCP+T |
menciptakan/memotong/
membungkuk sesuai dengan gambar klien |
/ |
6-70 |
NGN600 |
6-70 |
Kelas |
Ketebalan (mm) |
Kekuatan tensil/Mpa |
Naskh/% |
-20 nilai dampak longitudinal/J |
Kekerasan/HB |
NM360 |
<80 |
≥1100 |
≥12 |
≥24 |
330-390 |
|
<80 |
≥1200 |
≥10 |
≥24 |
370-430 |
|
<80 |
≥1250 |
≥7 |
≥24 |
420-480 |
NHOTEL |
<70 |
/ |
/ |
≥24 |
≥470 |
|
<70 |
/ |
/ |
/ |
≥530 |
NGN600 |
<60 |
/ |
/ |
/ |
≥570 |
Hasil pengujian pelat baja tahan aus |
Kelas |
Ketebalan (mm) |
Kekerasan/HB |
Kekuatan Tenkumuh/MPA |
Naskh (Nlonh) |
-20 nilai dampak longitudinal/J |
|
6 |
406 |
1280 |
16 |
76/87/65 |
|
20 |
404 |
1260 |
17.5 |
57/57/65 |
|
50 |
398 |
1300 |
25.5 |
40/35/45 |
|
80 |
417 |
1320 |
23.5 |
48/51/49 |
|
6 |
439 |
1320 |
23 |
43/38/30 |
|
20 |
448 |
1460 |
24 |
62/52/66 |
|
50 |
444 |
1340 |
21 |
35/37/40 |
|
80 |
454 |
1410 |
21.5 |
40/41/49 |
NHOTEL |
6 |
485 |
1653 |
11.5 |
33/26/32 |
NHOTEL |
20 |
505 |
1730 |
17.5 |
36/33/30 |
NHOTEL |
50 |
499 |
1569 |
16.5 |
42/38/32 |
NHOTEL |
70 |
488 |
1540 |
12.5 |
60/55/64 |
|
6 |
540 |
1853 |
10.5 |
/ |
|
20 |
545 |
1855 |
11.5 |
/ |
|
50 |
550 |
1900 |
10.5 |
/ |
|
70 |
545 |
1840 |
12 |
/ |
NGN600 |
6 |
575 |
/ |
/ |
/ |
NGN600 |
20 |
580 |
/ |
/ |
/ |
NGN600 |
50 |
582 |
/ |
/ |
/ |
NGN600 |
70 |
578 |
/ |
/ |
/ |
Pelat Resisant abrasi
Pelat baja keras
hard 500 keras 400
pelat baja potong dan tekukan
Produk dan
- Proses produksi
1)Bagan Alur proses pembuatan bagan
Furance+Hot Metal Cawan Tuang Truk+KR Hot Metal Treatment+Konverter+LF Furnace+RH Degassing Vakum+con-cast
2. Bagan Aliran proses Rolling
Memanaskan kembali Furnance+Pengeirapan Air bertekanan tinggi pembersih kerak+Edger+Peleburan+Pengakselerasi pabrik+Pengebata+Pengebata+menandai dan Pencetakan semprotan+tempat Tidur Pendingin+UT+Potong Shear+pemangkasan sisi Ganda+Tanda Potong-ke-Panjang+Pengukuran+Tanda dan semprotan Mencetak+Reeler dingin/Perawatan panas
3.Bagan Aliran Perawatan-panas
Pelat+Peledakan+Quenching Furance+Quencing Machine+tempering Furance+Reeler hangat+tempat Tidur King+Pemotong+Pengemasan Akhir&Penyaring
4.Ketebalan dan Lebar
Ketebalan:4,5mm-150mm
Lebar:1600mm-4100 mm
5.Kelas Utama
Jerman:XAR400,XAR450,XAR500,XAR600,DillDillawet,DillDillur500
BELGIA:QUALD400,QUALARD450,QUARD500
Prancis:FOR400,FO500,Creusabar00,Creuspembatalan
BAJA:B-HARROW,B-HARD400,B-HARROW,B-HARROW
HBIS:NM360,NHOTEL, NM450,GN500
FINLANDIA: RAEX400,RAEX450,RAEX500
JEPANG:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500
6.komposisi kimia&properti
Kelas |
c |
Si |
MN |
P |
S |
Al |
CR+Ni+Mo |
NB+V+Ti |
|
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 0.9 |
Lacak jumlah |
|
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 1.2 |
NHOTEL |
0.10-0.40 |
0.20-0.45 |
1.00-2.00 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 1.5 |
|
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 2.0 |
NGN600 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 2.5 |
XCHD400 |
0.10-0.30 |
0.20-0.40 |
1.00-2.00 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 0.1 |
XHD4650 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 0.9 |
XCHD500 |
0.10-0.40 |
0.20-0.45 |
1.00-2.00 |
Maks. 0.015 |
Maks. 0.003 |
Min 0.020 |
Maks. 1.5 |
7.
Kelas |
Ukuran (mm) |
RP0,2(Mpa) |
RM(Mpa) |
A50(%) |
AKV,(CELCIUS) |
KV2(J) |
HBW |
|
100 |
1233 |
1337 |
15 |
-20 |
35 |
37 |
42 |
415 |
|
60 |
1345 |
1434 |
9.5 |
-20 |
72 |
59 |
58 |
455 |
NHOTEL |
50 |
1608 |
1706 |
10.5 |
-20 |
43 |
50 |
45 |
495 |
XCHD400 |
35 |
1025 |
1161 |
17.5 |
-40 |
52 |
45 |
40 |
413 |
XHD4650 |
30 |
1281 |
1400 |
10.5 |
-40 |
45 |
48 |
52 |
453 |
XCH500 |
6 |
1465 |
1529 |
13.5 |
-40 |
24 |
24 |
22 |
515 |
8.Cersifikasi (Server)
9 masyarakat Klasifikasi
Bersertifikat ISO 9001
9.Kemasan Pengiriman
Pengemasan yang layak dengan kontainer atau kapal kargo besar
Deliediakan setiap kali:ukuran stok dalam 7 hari;materi baru dalam 40 hari
10.Layanan kami
Kita dapat memotong dan menekuk pelat baja sesuai kebutuhan pelanggan requrement atau menggambar,pengemasan sesuai permintaan pelanggan
11.Aplikasi
Dengan mengadopsi desain komposisi kimia gabungan dari low karbon,low sulfur,low fosfor dan aloi mikro, dengan menerapkan penggalian offline dan teknologi otomatisasi canggih lainnya,pelat tahan aus (Abrasi Resisant) populer di rumah dan di luar negeri. Digunakan terutama untuk Pabrik Daya Termal, Mines Batu Bara, Cement Mill, Loading Machinery,Mining Machinery.Metalurgi Machinery,pelat tahan Aus juga dapat digunakan dalam Cangkerang, Vane, suku Cadang Mekanis yang digunakan di halaman dan port, Komponen Struktur bantalan, dll.
PELAT BAJA/PELAT BAJA/LEMBARAN BAJA/PELAT BAJA TAHAN AUS