Tipe: | Pelat Baja |
---|---|
Standar: | AISI, ASTM, DIN, JIS, GB |
Komposisi: | pelat baja campuran |
Teknik: | Gulungan yang panas |
Bentuk: | Pelat |
Perlakuan Permukaan: | black sruface atau dicat |
Pemasok dengan izin usaha terverifikasi
Kelas | c | Si | MN | P | S | Al | CR+Ni+Mo | NB+V+Ti |
0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 0.9 | Lacak jumlah | |
0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 1.2 | ||
NHOTEL | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 1.5 | |
0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 2.0 | ||
NGN600 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 2.5 | |
XCHD400 | 0.10-0.30 | 0.20-0.40 | 1.00-2.00 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 0.1 | |
XHD4650 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 0.9 | |
XCHD500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Maks. 0.015 | Maks. 0.003 | Min 0.020 | Maks. 1.5 |
Hasil pengujian pelat baja tahan aus | |||||
Kelas | Ketebalan (mm) | Kekerasan/HB | Kekuatan Tenkumuh/MPA | Naskh (Nlonh) | -20 nilai dampak longitudinal/J |
6 | 406 | 1280 | 16 | 76/87/65 | |
20 | 404 | 1260 | 17.5 | 57/57/65 | |
50 | 398 | 1300 | 25.5 | 40/35/45 | |
80 | 417 | 1320 | 23.5 | 48/51/49 | |
6 | 439 | 1320 | 23 | 43/38/30 | |
20 | 448 | 1460 | 24 | 62/52/66 | |
50 | 444 | 1340 | 21 | 35/37/40 | |
80 | 454 | 1410 | 21.5 | 40/41/49 | |
NHOTEL | 6 | 485 | 1653 | 11.5 | 33/26/32 |
NHOTEL | 20 | 505 | 1730 | 17.5 | 36/33/30 |
NHOTEL | 50 | 499 | 1569 | 16.5 | 42/38/32 |
NHOTEL | 70 | 488 | 1540 | 12.5 | 60/55/64 |
6 | 540 | 1853 | 10.5 | / | |
20 | 545 | 1855 | 11.5 | / | |
50 | 550 | 1900 | 10.5 | / | |
70 | 545 | 1840 | 12 | / | |
NGN600 | 6 | 575 | / | / | / |
NGN600 | 20 | 580 | / | / | / |
NGN600 | 50 | 582 | / | / | / |
NGN600 | 70 | 578 | / | / | / |