Proses...........................................Cat yang dihasilkan oleh proses sulfat (Sulate process)
Perlakuan ke permukaan............................ .... ZrO, Al O, spesialisasi Substains
Klasifikasi standar(ISO591-1)........................................................................................................................................................................ R2
Gravitasi spesifik(ISO787-10).......................................................... 4,0g/cm3
Konten TiO2(ISO591-1)............................................................................. ........ ≥93.0%
105tercelcius tidak stabil di bawah paket(ISO787-2).......................... ≤0.5%
Bahan larut (ISO787-2)........................................................................................................................................................................................................................ ≤0.5%
Residu pada saringan(45µm)(ISO787-18).............................................................................................................................................................................................................................. ≤0.1%
Nilai transformasi ubin............................................................................. ≥98%
Kondisi aplikasi
Bubuk Terputih(L*)...................................................................................................................................................................................................................................................................................................................... 98-98.5
Hue(b*)............................................................................................................... 2.2-2.5
Kekuatan penyebaran relatif (ISO787-24).......................dekat dengan sampel (95-105)%
Warna dalam sistem warna(ISO787-25)..............dekat dengan sampel colorΔE≤0.3
Nilai PH suspensi aqua (ISO787-9)............................................ 6.5-8.5
Volume penyerapan oli (ISO787-5)...................................................................................... ≤22 g/100 g
Resistivitas ekstrak aquaceous(ISO787-14)................................... ≥100Ω.M.
Dispersi dengan kecepatan tinggi di dalam campuran Meyydsystem......................... ≤35µm
Pengemasan:
N.25 KG plastik dan kantong kertas
![Zirconia and Alumina Treated Rutile Titanium Dioxide](//www.micstatic.com/athena/img/transparent.png)
![Zirconia and Alumina Treated Rutile Titanium Dioxide](//www.micstatic.com/athena/img/transparent.png)
![Zirconia and Alumina Treated Rutile Titanium Dioxide](//www.micstatic.com/athena/img/transparent.png)