Type: | Pond Liner |
---|---|
Ceiling Tile Shape: | Roll |
Material: | HDPE |
Thickness: | 2.0mm |
Ceiling Tile Type: | HDPE |
Surface Treatment: | Pond Liner |
Pemasok dengan izin usaha terverifikasi
Properti | Nilai uji | ||||
0,75mm | 1.00 mm | 1.50 mm | 2.00 mm | ||
Ketebalan - mils (min. ave.)· dengan nilai terendah 10 | nom. (mil)-10% | nom. (mil)-10% | nom. (mil)-10% | nom. (mil)-10% | |
Kerapatan (min.) | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | |
Properti tensil (1) (min. ave.) · menghasilkan kekuatan · kekuatan pecah · keuntungan · pengeluaran istirahat |
11 kN/m 20 kN/m 12% 700% |
15 kN/m 27 kN/m 12% 700% |
22 kN/m 40 kN/m 12% 700% |
29 kN/m 53 kN/m 12% 700% |
|
Resistansi robek (min ave.) | 93N | 125 N. | 187 N. | 249 N. | |
Resistansi kebocoran (min. ave.) | 240N | 320 N. | 480 N. | 640 N. | |
Resistansi terhadap retakan tegangan (2) | 300 jam | 300 jam | 300 jam | 300 jam | |
Konten Hitam Karbon - % | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | |
Karbon Black Dispersion | catatan (4) | catatan (4) | catatan (4) | catatan (4) | |
Waktu Orientasi Oksidatif (OIT) (min ave.) (5) (A) Standar OIT- atau - (B) Tekanan Tinggi OIT |
100 mnt 400 mnt |
100 mnt 400 mnt |
100 mnt 400 mnt |
100 mnt 400 mnt |
|
Usia oven pada 85 derajat C (5), (6) (A) Standard OIT (min. ave.) - % dipertahankan setelah 90 hari atau - (B) Tekanan Tinggi OIT (min. ave.) - % dipertahankan setelah 90 hari |
55% 80% |
55% 80% |
55% 80% |
55% 80% |
|
Resistansi UV (7) (A) Standard OIT (min. ave.) - atau - (B) Tekanan Tinggi OIT (min. ave.) - % dipertahankan setelah 1600 jam |
N.R. (8) 50% |
N.R. (8) 50% |
N.R. (8) 50% |
N. R. (8) 50%v |