9.52mm size auto parts fuel tube with Zinc coating
Basic information of auto parts fuel tube
| Product Name | Double Wall Welded Bundy Tube |
| Standard | WSS-M21P30-A2 - FORD standard |
| Size | Ф4.76*0.7, Ф6*0.7, Ф6.35*0.7, Ф9.52*0.7, Ф10*0.7, Ф10*1.0 , Ф12*0.7 Ф12*1.0 |
| Surface Treatment | Galvanization: white zinc, Olive-drab zinc, Celadon zinc, colored zinc; PVF coated, PA12(Nylon) coated, ALGAL |
| Material | Low Carbon Steel/Bao Steel Bhg2, copper |
| Length | Cut to length, Any length as your requirements |
| Packing | Coils or Bundles ,then in pallets or wooden boxes |
| Delivery time | Within 30 days(Order quantity is between 2 Metric Tons and 5 Metric Tons) |
| Other situation can be followed the negotiation by two parties |
| Main use | Widely used in braking & power steering tube system and fuel tube system etc |
| Factory | 24 digital tube making lines, 7 surface treatment lines, 2500 Tons/Year, FORD executive standard and 30 years of manufacture experience. |
| MOQ | Can negotiated by mutual agreement |
Inspection Report of auto parts fuel tube
| No | Inspection items | unit | Standard |
| 1 | Zinc plated | µm | 6 / 13 / 25 |
| 2 | Coated thickness | µm | >=120 |
| 3 | Tensile strength | Mpa | >=290 |
| 4 | Yield strength | Mpa | >=170 |
| 5 | Elongation | % | >=14 |
| 6 | Inner cleanliness | g/m2 | <=0.2 |
| 7 | Burst pressure | Mpa | 55 |
| 8 | Pressurs resistance | Mpa | 19.6 |
Test of auto parts fuel tube
Bending test:
Bend the tube 360º over a mandrel of 3 times, the diameter no kinking, cracking or other defect.
Flaring test:
Increase the OD 25% with the flaring reshed of the 1:10 spindle taper, no broken or crack
Flatten test:
GB/T 241
The weld shall be placed at 90º from the direction of applied force, no crack or flaw when flattened between parallel plates to a distance equal to three times the wall thickness.
Pressure-resistant properties:
Keep in 41.2MPa pressure for 5 minutes, no burst or leakage phenomenon.
Water resistance:
Soaked in 40 ºC distilled water for 240h, no red rust and blistering.
Liquid resistance:
Respectively soaked in brake fluid, power steering fluid, motor oil at 50 +/- 2 °C and soaked in 35% sulphuric acid, gasoline (unleaded), anti-freezer, windshield washer at 23 +/- 2 °C for 504 hours. No lifting and blistering
coating should be evident at knife cut under 10X magnification
1. No scribed samples:
Assessing after gravelometer test. Then do 2000h salt spray test, and then do burst pressure test. The burst value should be more than 80% of original value.
2. Scribed samples:
2000h salt spray test, then do burst pressure test. All the burst value should be more than 80% of original value.
Salt Spray test: over 2000-3000 hours without red rust
PS: We are under FORD executive standard, but we can do adjustment to satisfy clients' product
technical requirement.
Any inquire Pls feel free to contact us, we will give feedback in 24 hours.
Alamat:
No. 127 Dongfang Avenue, Jingzhou High-Tech Development Zone, Hubei, China
Jenis Usaha:
Produsen/Pabrik, Perusahaan Perdagangan
Jangkauan Bisnis:
Mesin Manufaktur & Pemrosesan, Mobil, Suku Cadang Motor & Aksesoris, Perkakas & Hardware
Pengenalan Perusahaan:
Perusahaan kami menyediakan berbagai jenis produk. Kualitas tinggi dan harga yang bagus. Kami senang untuk melakukan penyelidikan Anda dan kami akan kembali lagi ke sana sesegera mungkin. Kita memegang prinsip "kualitas yang pertama, layanan yang diberikan terlebih dahulu, perbaikan berkelanjutan dan inovasi untuk memenuhi pelanggan" untuk manajemen dan "cacat nol, keluhan nol" sebagai sasaran kualitas. Untuk layanan sempurna, kami menyediakan produk dengan kualitas yang baik dengan harga yang wajar.