Type: | Alloy Seamless Steel Pipe |
---|---|
Standard: | AISI, ASTM, DIN, JIS, GB, BS |
Composition: | Ferrous Steel Scrap |
Technique: | Cold Drawn |
Shape: | Pipe |
Surface Treatment: | Black/Varnishing/Polished/Antiseptical/Oiled...... |
Pemasok dengan izin usaha terverifikasi
GB5310 (2008) - Tabung baja tanpa sambungan untuk perebus tekanan tinggi (GB)
ASTM A333 (2004) - temperatur rendah dengan tabung baja yang mulus (American Standard)
ASTM A335 (2006) - Temperatur tinggi untuk Campuran Ferritic yang lancar Pipa baja (Standar Amerika)
- pipa baja bebas panas tanpa sambungan yang tahan panas (standar Jerman)
EN10216-2 - Penggunaan standar perpipaan Tekanan Eropa
Komposisi kimia:
Standar |
Kelas |
Komposisi kimia(%) |
||||||
C |
Si |
MN |
P |
S |
CR |
MO |
||
GB5310 |
20MnG |
0.17-0.23 |
0.17-0.37 |
0.70-1.00 |
≤0.025 |
≤0.015 |
≤0.25 |
≤0.15 |
25MnG |
0.23-0.27 |
0.17-0.37 |
0.70-1.00 |
≤0.025 |
≤0.015 |
≤0.25 |
≤0.15 |
|
15CMoG |
0.12-0.18 |
0.17-0.37 |
0.40-0.70 |
≤0.025 |
≤0.015 |
0.80-1.10 |
0.40-0.55 |
|
12C2MoG |
0.08-0.15 |
≤0.50 |
0.40-0.60 |
≤0.025 |
≤0.015 |
2.00-2.50 |
0.90-1.13 |
|
12C1MoVG |
0.08-0.15 |
0.17-0.37 |
0.40-0.70 |
≤0.025 |
≤0.010 |
0.90-1.20 |
0.25-0.35 |
|
10C9Mo1VNbN |
0.08-0.12 |
0.20-0.50 |
0.30-0.60 |
≤0.020 |
≤0.010 |
8.00-9.50 |
0.85-1.05 |
|
ASTM A335 |
P11 |
0.05-0.15 |
0.50-1.0 |
0.30-0.60 |
≤0.030 |
≤0.030 |
1.00-1.50 |
0.50-1.00 |
12 |
0.05-0.15 |
≤0.50 |
0.30-0.61 |
≤0.030 |
≤0.030 |
0.80-1.25 |
0.44-0.65 |
|
P22 |
0.05-0.15 |
≤0.50 |
0.30-0.60 |
≤0.030 |
≤0.030 |
1.90-2.60 |
0.87-1.13 |
|
P5 |
≤0.15 |
≤0.50 |
0.30-0.60 |
≤0.030 |
≤0.030 |
4.00/6.00 |
0.45/0.65 |
|
91 |
0.08-0.12 |
0.20-0.50 |
0.30-0.60 |
≤0.020 |
≤0.010 |
8.00-9.50 |
0.85-1.05 |
|
P92 |
0.07-0.13 |
≤0.50 |
0.30-0.60 |
≤0.020 |
≤0.010 |
8.50-9.50 |
0.30-0.60 |
|
DIN 17175 |
|
≤0.21 |
0.10-0.35 |
0.40-1.20 |
≤0.040 |
≤0.040 |
|
|
15Mo3 |
0.12-0.20 |
0.10-0.35 |
0.40-0.80 |
≤0.035 |
≤0.035 |
|
0.25-0.35 |
|
13CrMo44 |
0.10-0.18 |
0.10-0.35 |
0.40-0.70 |
≤0.035 |
≤0.035 |
0.70-1.10 |
0.45-0.65 |
|
10CMo910 |
0.08-0.15 |
≤0.50 |
0.40-0.70 |
≤0.035 |
≤0.035 |
2.00-2.50 |
0.90-1.20 |
|
EN1021 6-2 |
15KCuBNb5-6-4 (WB36) |
≤0.17 |
0.25-0.50 |
0.80-1.20 |
≤0.025 |
≤0.020 |
≤0.30 |
0.25-0.50 |
Standar |
Kelas |
Komposisi kimia(%) |
||||||
CU |
NI |
V |
Alt |
W |
Jml |
N |
||
GB5310 |
20MnG |
≤0.20 |
≤0.25 |
≤0.08 |
|
|
|
|
25MnG |
≤0.20 |
≤0.25 |
≤0.08 |
|
|
|
|
|
15CMoG |
≤0.20 |
≤0.30 |
|
|
|
|
|
|
12C2MoG |
≤0.20 |
≤0.30 |
|
|
|
|
|
|
12C1MoVG |
≤0.20 |
≤0.30 |
0.15-0.30 |
|
|
|
|
|
10C9Mo1VNbN |
≤0.20 |
≤0.40 |
0.18-0.25 |
≤0.020 |
|
0.06-0.10 |
0.03-0.07 |
|
ASTM A335 |
P11 |
|
|
|
|
|
|
|
12 |
|
|
|
|
|
|
|
|
P22 |
|
|
|
|
|
|
|
|
P5 |
|
|
|
|
|
|
|
|
91 |
|
≤0.40 |
0.18-0.25 |
≤0.015 |
|
0.06-0.10 |
0.03-0.07 |
|
P92 |
B0,001 0.006 |
≤0.40 |
0.15-0.25 |
≤0.015 |
1.50-2.00 |
0.04-0.09 |
0.03-0.07 |
|
DIN 17175 |
|
|
|
|
|
|
|
|
15Mo3 |
|
|
|
|
|
|
|
|
13CrMo44 |
|
|
|
|
|
|
|
|
10CMo910 |
|
|
|
|
|
|
|
|
EN1021 6-2 |
15KCuBNb5-6-4 (WB36) |
0.50-0.80 |
1.00-1.30 |
|
≤0.05 |
|
0.015-0.045 |
|
Properti Mekanis:
Standar |
Kelas |
Kekuatan tensil (MPa) |
Kekuatan yield (MPa) |
Naskh (penghapusan) (%) |
Impact work(J) |
Kekerasan |
GB5310 |
20MnG |
≥415 |
≥240 |
≥22 |
≥35 |
|
25MnG |
≥485 |
≥275 |
≥20 |
≥35 |
|
|
15CMoG |
44040-640 |
≥235 |
≥21 |
≥35 |
|
|
12C2MoG |
450-600 |
≥280 |
≥20 |
≥35 |
|
|
12C1MoVG |
47040-640 |
≥255 |
≥21 |
≥35 |
|
|
10C9Mo1VNbN |
≥585 |
≥415 |
≥20 |
≥35 |
|
|
ASTM A333 |
A333 Gr1 |
≥380 |
≥205 |
≥28 |
-45≥18 |
|
A333 Gr6 |
≥415 |
≥240 |
≥22 |
-45≥18 |
|
|
ASTM A335 |
P11 |
≥415 |
≥205 |
≥22 |
≥35 |
≤163HB |
12 |
≥415 |
≥220 |
≥22 |
≥35 |
≤163HB |
|
P22 |
≥415 |
≥205 |
≥22 |
≥35 |
≤163HB |
|
P5 |
≥415 |
≥205 |
≥22 |
≥35 |
≤187HB |
|
91 |
585-760 |
≥415 |
≥20 |
≥35 |
≤250HB |
|
P92 |
≥620 |
≥440 |
≥20 |
≥35 |
250HB |
|
|
ST45,8/III |
410530 hingga |
≥255 |
≥21 |
≥27(DVM) |
|
15Mo3 |
450-600 |
≥270 |
≥22 |
≥34(DVM) |
|
|
13CrMo44 |
4405-590 |
≥290 |
≥22 |
≥34(DVM) |
|
|
10CMo910 |
480-630 |
≥280 |
≥20 |
≥34(DVM) |
|
|
EN10216-2 |
15KCuBNb5-6-4 (WB36) |
610-780 |
≥440 |
≥19 |
≥40 |
MOQ | 1 ton |
Contoh | Sampel tersedia |
Ketentuan Pembayaran | L/C,T/T. |
Jangka waktu perdagangan | FOB, CFR, CIF |
Port | Shanghai, Tianjin, Qingdao |
Paket |
|
Tanda | (a) tanpa tanda, (b) ditandai dengan garis berwarna pada tabung (bundel tabung), (c) ditandai dengan semprotan, baik dengan warna putih atau hitam menggunakan inkjet, (d) ditandai dengan membubuhkan data (ini berlaku untuk OD > 22 mm dan WT >2.3 mm). |
Perlindungan Permukaan | Tersedia antar kertas Tersedia film dengan perlindungan PVC Tip: Ketika memesan, metode dan cara untuk melindungi permukaan tabung selama pengangkutan dan penyimpanan harus sesuai untuk sementara waktu. |