Aloi | Kelas | komposisi kimia % | |||||
Mg | Al | ZN | MN | CE | ZR | ||
Mg | Mg99.95 | ≥99.95 | ≤0.01 | - | ≤0.004 | - | - |
Mg99,50 | ≥99.5 | - | - | - | - | - | |
Mg99,00 | ≥99.0 | - | - | - | - | - | |
MgSO AlZn | Az31B | BAL. | 2.5-3.5 | 0.60-1.4 | 0.20-1.0 | - | - |
AZ31S | BAL. | 2.4-3.6 | 0.50-1.5 | 0.15-0.40 | - | - | |
AZ31T | BAL. | 2.4-3.6 | 0.50-1.5 | 0.05-0.04 | - | - | |
AZ40M | BAL. | 3.0-4.0 | 0.20-0.80 | 0.15-0.50 | - | - | |
Az41M | BAL. | 3.7-4.7 | 0.80-1.4 | 0.30-0.60 | - | - | |
AZ61A | BAL. | 5.8-7.2 | 0.40-1.5 | 0.15-0.50 | - | - | |
AZ80A | BAL. | 7.8-9.2 | 0.20-0.80 | 0.12-0.50 | - | - | |
Az80M | BAL. | 7.8-9.2 | 0.20-0.80 | 0.15-0.50 | - | - | |
AZ80S | BAL. | 7.8-9.2 | 0.20-0.80 | 0.12-0.40 | - | ||
Az91D | BAL. | 8.5-9.5 | 0.45-0.90 | 0.17-0.40 | - | - | |
MgSO | M1C | BAL. | ≤0.01 | - | 0.50-1.3 | - | - |
M2M | BAL. | ≤0.20 | ≤0.30 | 1.3-2.5 | - | - | |
M2S | BAL. | - | - | 1.2-2.0 | - | - | |
MgZnZr | Zk61M | BAL. | ≤0.05 | 5.0-6.0 | ≤0.10 | - | 0.30-0.90 |
Zk61S | BAL. | - | 4.8-6.2 | - | - | 0.45-0.80 | |
Mgitaire | Me20M | BAL. | ≤0.020 | ≤0.30 | 1.3-2.2 | - | - |
Kelas | Kondisi | Diameter/mm | RM/MPa dengan kekuatan tensil | Rp0,2/Mpa | Naskh A/% |
AZ31B | H112 | ≤130 | 220 | 140 | 7.0 |
AZ40M | H112 | ≤100 | 245 | - | 6.0 |
100-130 | 245 | - | 5.0 | ||
Az41M | H112 | ≤130 | 250 | - | 5.0 |
AZ61A | H112 | ≤130 | 260 | 160 | 6.0 |
AZ61M | H112 | ≤130 | 265 | - | 8.0 |
Az80A |
H112 | ≤60 | 295 | 195 | 6.0 |
60-130 | 290 | 180 | 4.0 | ||
T5 | ≤60 | 325 | 205 | 4.0 | |
60-130 | 310 | 205 | 2.0 | ||
ME20M |
H112 |
≤50 | 215 | - | 4.0 |
50-100 | 205 | - | 3.0 | ||
100-130 | 195 | - | 2.0 | ||
ZK61M | T5 | ≤100 | 315 | 245 | 6.0 |
100-130 | 305 | 235 | 6.0 | ||
Zk61S | T5 | ≤130 | 310 | 230 | 5.0 |
Numi | Kelas | komposisi kimia % | |||||
Al | ZN | MN | Si | Mg | |||
1 | YZMgSO4 Si | YM102 | 1.9-2.5 | ≤0.20 | 0.20-0.60 | 0.7-1.20 | BAL. |
2 | YZMgSO4 Si (B) | YM103 | 1.9-2.5 | ≤0.25 | 0.05-0.15 | 0.70-1.20 | BAL. |
3 | YZMgSO Aly(A) | YM104 | 3.7-4.8 | ≤0.10 | 0.22-0.48 | 0.60-1.40 | BAL. |
4 | YZMgSO Alpary(B) | YM105 | 3.7-4.8 | ≤0.10 | 0.35-0.60 | 0.60-1.40 | BAL. |
5 | YZMgSO Al4Si(S) | YM106 | 3.5-5.0 | ≤0.20 | 0.18-0.70 | 0.5-1.5 | BAL. |
6 | YZMgSO Alpar2 | YM202 | 1.6-2.5 | ≤0.20 | 0.33-0.70 | ≤0.08 | BAL. |
7 | YZMgSO 5Mn | YM203 | 4.5-5.3 | ≤0.20 | 0.28-0.50 | ≤0.08 | BAL. |
8 | YZMgSO 6Mn(A) | YM204 | 5.6-6.4 | ≤0.20 | 0.15-0.50 | ≤0.20 | BAL. |
9 | YZMgSO 6Mn | YM205 | 5.6-6.4 | ≤0.20 | 0.26-0.50 | ≤0.08 | BAL. |
10 | YZMgSO 8Zn1 | YM302 | 7.0-8.1 | 0.40-1.00 | 0.13-0.35 | ≤0.30 | BAL. |
11 | YZMgSO 9Zn1(A) | YM303 | 8.5-9.5 | 0.45-0.90 | 0.15-0.40 | ≤0.20 | BAL. |
12 | YZMgSO 9Zn1(B) | YM304 | 8.5-9.5 | 0.45-0.90 | 0.15-0.40 | ≤0.20 | BAL. |
13 | YZMgSO4 Alzk1(D) | YM305 | 8.5-9.5 | 0.45-0.90 | 0.17-0.40 | ≤0.08 | BAL. |
Kelas | komposisi kimia/% | ||||||||||||||
Mg | Al | ZN | MN | RE | ZR | AG | Y | Li | Be | Si | FE | CU | NI | lainnya | |
ZK51A | BAL. | - | 3.8-5.3 | - | - | 0.3-1.0 | - | - | - | - | ≤0.01 | - | ≤0.03 | ≤0.01 | ≤0.03 |
Zk61A | BAL. | - | 5.7-6.3 | - | - | 0.3-1.0 | - | - | - | - | ≤0.01 | - | ≤0.03 | ≤0.01 | ≤0.03 |
K1A | BAL. | - | - | - | - | 0.3-1.0 | - | - | - | - | ≤0.01 | - | ≤0.03 | ≤0.01 | ≤0.03 |
Zk41A | BAL. | - | 3.7-4.8 | ≤0.15 | 1.0-1.75 | 0.3-1.0 | - | - | - | - | ≤0.01 | ≤0.01 | ≤0.03 | ≤0.005 | ≤0.03 |
EZ33A | BAL. | - | 2.0-3.0 | ≤0.15 | 2.6-3.9 | 0.3-1.0 | - | - | - | - | ≤0.01 | ≤0.01 | ≤0.03 | ≤0.005 | ≤0.03 |
QE22A | BAL. | - | ≤0.20 | ≤0.15 | 1.9-2.4 | 0.3-1.0 | 2.0-3.0 | - | - | - | ≤0.01 | - | ≤0.03 | ≤0.01 | ≤0.03 |
QE22S | BAL. | - | ≤0.20 | ≤0.15 | 2.0-3.0 | 0.1-1.0 | 2.0-3.0 | - | - | - | ≤0.01 | ≤0.01 | ≤0.03 | ≤0.005 | - |
EQ21A | BAL. | - | - | - | 1.5-3.0 | 0.3-1.0 | 1.3-1.7 | - | - | - | ≤0.01 | - | 0.05-0.1 | ≤0.01 | ≤0.03 |
EQ21S | BAL. | - | ≤0.20 | ≤0.15 | 1.5-3.0 | 0.1-1.0 | 1.3-1.7 | - | - | - | ≤0.01 | ≤0.01 | 0.05-0.1 | ≤0.005 | - |
WE54A | BAL. | - | ≤0.20 | ≤0.15 | 1.5-4.0 | 0.3-1.0 | - | 4.75-5.5 | ≤0.2 | - | ≤0.01 | ≤0.01 | ≤0.03 | ≤0.005 | ≤0.03 |
BAL. | - | ≤0.20 | ≤0.15 | 2.4-4.4 | 0.3-1.0 | - | 3.7-4.3 | ≤0.2 | - | ≤0.01 | ≤0.01 | ≤0.03 | ≤0.005 | ≤0.03 |
AZ31 | GB/T 5153 | |||||||
Elemen | Al | ZN | MN | Si | FE | CU | NI | Lainnya, total |
Min% | 2.40 | 0.50 | 0.15 | |||||
Maks.% | 3.60 | 1.50 | 0.4 | 0.10 | 0.005 | 0.05 | 0.005 | 0.3 |
AZ61 | GB/T 5153 | |||||||
Elemen | Al | ZN | MN | Si | FE | CU | NI | Lainnya, total |
Min% | 5.50 | 0.5 | 0.15 | |||||
Maks.% | 6.50 | 1.50 | 0.40 | 0.10 | 0.005 | 0.05 | 0.005 | 0.3 |
AZ91 | GB/T 5153 | ||||||||
Elemen | Al | ZN | MN | Si | FE | CU | NI | Be | Lainnya, total |
Min% | 8.5 | 0.45 | 0.17 | 0.0005 | |||||
Maks.% | 9.5 | 0.90 | 0.40 | 0.08 | 0.004 | 0.025 | 0.001 | 0.003 | 0.3 |
AZ92 | AWS A5,19-1992 | ||||||||
Elemen | Al | ZN | MN | Si | FE | CU | NI | Be | Lainnya, total |
Min% | 8.3 | 1.7 | 0.15 | 0.0002 | |||||
Maks.% | 9.7 | 2.3 | 0.50 | 0.05 | 0.005 | 0.05 | 0.005 | 0.0008 | 0.3 |