PARAMETER TEKNIS
TIDAK | Item Teks | Satuan | Kinerja | Hasil teks | Metode Teks | ||
Bahan Belakang | |||||||
1 | Strengt tensil | MPa | ≥17 | 19.47 | ASTM D638 | ||
2 | Panjang | % | ≥400 | 626 | ASTM D638 | ||
3 | Lakukan Vicat lembek | ≥90 | 92 | ASTM D1525 | |||
4 | Brittatur | <-65 | <-65 | ASTM D2671C | |||
5 | Strengt elektrik | MV/m | ≥25 | 33.13 | ASTM D149 | ||
6 | Volume Resativa | Ω.m | ≥1*1013 | 1.1*1013 | ASTM D257 | ||
7 | Kerac stres Lingkungan | h | ≥1000 | >1000 | GB/T1842 | ||
8 |
Kimia resistance (7d |
10% HCI |
Kekuatan tensil | MPa | ≥85 | 104.9 | ASTM D638 |
Naskh (Naskh) | % | ≥85 | 96.3 | ASTM D638 | |||
10% Naah |
Kekuatan tensil | MPa | ≥85 | 102.1 | ASTM D638 | ||
Naskh (Naskh) | % | ≥85 | 95.6 | ASTM D638 | |||
10% NaCl |
Kekuatan tensil | MPa | ≥85 | 108.3 | ASTM D638 | ||
Naskh (Naskh) | % | ≥85 | 94.1 | ASTM D638 | |||
9 | Proses menua (150 C,168h |
Kekuatan tensil | MPa | ≥14 | 20.7 | ASTM D638 | |
Naskh (Naskh) | % | ≥300 | 630 | ASTM D638 |
TIDAK. | Text | Uni | Performa | Ketahanan Teks | Metode Teks | |
Perekat | ||||||
1 | Melembutkan | ≥90 | 90.1 | ASTM E28 | ||
2 | Brittatur | <-15 | <-15 | ASTM D2671C | ||
3 | Lap Shea | MPa | ≥1.0 | 1.5 | ASTM D1002 | |
4 |
Kekuatan robek (23±2 DERAJAT |
Baja | N/cm | ≥70 | 145.6 | ASTM D1000 |
Primer | N/cm | ≥70 | 205.9 | ASTM D1000 | ||
PE lor | N/cm | ≥70 | 190.0 | ASTM D1000 | ||
Epoksi tidak pelarut | ||||||
5 | Shear primer baru berhasil dipulihkan | MPa | ≥5.0 | 12 | SY/T0041 |