TIDAK | Item Teks | Satuan | Kinerja | Hasil teks | Metode Teks | ||||||||
Bahan Belakang | |||||||||||||
1 | Kekuatan tensil | MPa | ≥17 | 19.47 | ASTM D638 | ||||||||
2 | Naskh (Naskh) | % | ≥400 | 626 | ASTM D638 | ||||||||
3 | Vicat lunak poin | ≥90 | 92 | ASTM D1525 | |||||||||
4 | Suhu Britlerakan | <-65 | <-65 | ASTM D2671C | |||||||||
5 | Kekuatan dielektrik | MV/m | ≥25 | 33.13 | ASTM D149 | ||||||||
6 | Kepekaan volume | Ω.m | ≥1*1013 | 1.1*1013 | ASTM D257 | ||||||||
7 | Retakan Tekanan Lingkungan | h | ≥1000 | >1000 | GB/T1842 | ||||||||
8 |
Ketahanan Bahan kimia (7d) | 10% HCI | Kekuatan tensil | MPa | ≥85 | 104.9 | ASTM D638 | ||||||
Naskh (Naskh) | % | ≥85 | 96.3 | ASTM D638 | |||||||||
10% Naah | Kekuatan tensil | MPa | ≥85 | 102.1 | ASTM D638 | ||||||||
Naskh (Naskh) | % | ≥85 | 95.6 | ASTM D638 | |||||||||
10% NaCl | Kekuatan tensil | MPa | ≥85 | 108.3 | ASTM D638 | ||||||||
Naskh (Naskh) | % | ≥85 | 94.1 | ASTM D638 | |||||||||
9 | Penuaan termal (150,168h) | Kekuatan tensil | MPa | ≥14 | 20.7 | ASTM D638 | |||||||
Naskh (Naskh) | % | ≥300 | 630 | ASTM D638 | |||||||||
TIDAK | Item Teks | Satuan | Kinerja | Hasil teks | Metode Teks | ||||||||
Perekat | |||||||||||||
1 | Lap | MPa | ≥1.0 | 1.5 | ASTM D1002 | ||||||||
2 | Titik melemah | ≥90 | 90.1 | ASTOASME28 | |||||||||
3 | Suhu Britlerakan | <-15 | <-15 | ASTM D2671C | |||||||||
4 | Kupas kekuatan(23+/-2 ) | Baja | N/cm | ≥70 | 145.6 | ASTM D1000 | |||||||
Primer | N/cm | ≥70 | 205.9 | ASTM D1000 | |||||||||
Lapisan PE | N/cm | ≥70 | 190.0 | ASTM D1000 |