Tipe: | Elektrode grafit |
---|---|
Komposisi: | Sic |
Konten Karbon: | High-Carbon (Karbon Tinggi) |
Kelas: | UHP |
Cara membentuk: | Tampilan luas |
Morfologi kristal: | Serpihan Graphite |
Pemasok dengan izin usaha terverifikasi
Elektrode RP Graphite | Satuan |
Φ75-300 | Φ400-450 | Φ500-700 | |
Resistance≤ | Elektrode | ΜΩ·M. | 8.0 | 8.0 | 8.0 |
Puting payudara | 5.5 | 5.5 | 5.5 | ||
Kekuatan Meliuk≥ | Elektrode | MPa | 8.4 | 7.5 | 7.0 |
Puting payudara | 16.0 | 16.0 | 16.0 | ||
Elastis≤ | Elektrode | IPK | 8.0 | 8.0 | 8.0 |
Puting payudara | 12.0 | 12.0 | 12.0 | ||
Abu ≤ | Elektrode | % | 0.2 | 0.2 | 0.2 |
Puting payudara | 0.2 | 0.2 | 0.2 | ||
Kepadatan Massal≥ | Elektrode | G/cm³ | 1.60 | 1.60 | 1.60 |
Puting payudara | 1.75 | 1.75 | 1.75 | ||
(C. T E)≤ | Elektrode | 10-6/ | 2.8 | 2.8 | 2.8 |
Puting payudara | 2.7 | 2.7 | 2.7 |
Elektrode HP Graphite | Satuan |
Φ300-400 | Φ450-500 | Φ550-700 | |
Resistance≤ | Elektrode | ΜΩ·M. | 6.2 | 6.2 | 6.2 |
Puting payudara | 4.3 | 4.3 | 4.3 | ||
Kekuatan Meliuk≥ | Elektrode | MPa | 11.0 | 10.5 | 9.0 |
Puting payudara | 18.0 | 18.0 | 18.0 | ||
Elastis≤ | Elektrode | IPK | 9.0 | 9.0 | 9.0 |
Puting payudara | 13.0 | 13.0 | 13.0 | ||
Abu ≤ | Elektrode | % | 0.2 | 0.2 | 0.2 |
Puting payudara | 0.2 | 0.2 | 0.2 | ||
Kepadatan Massal≥ | Elektrode | G/cm³ | 1.68 | 1.68 | 1.68 |
Puting payudara | 1.77 | 1.77 | 1.77 | ||
(C. T E)≤ | Elektrode | 10-6/ | 2.0 | 2.0 | 2.0 |
Puting payudara | 1.8 | 1.8 | 1.8 |
Elektrode UHP Graphite | Satuan |
Φ300-400 | Φ450-500 | Φ550-700 | |
Resistance≤ | Elektrode | ΜΩ·M. | 5.5 | 5.5 | 5.5 |
Puting payudara | 3.8 | 3.8 | 3.8 | ||
Kekuatan Meliuk≥ | Elektrode | MPa | 12.0 | 12.0 | 12.0 |
Puting payudara | 22.0 | 22.0 | 24.0 | ||
Elastis≤ | Elektrode | IPK | 8.0 | 8.0 | 8.0 |
Puting payudara | 17.0 | 17.0 | 17.0 | ||
Abu ≤ | Elektrode | % | 0.2 | 0.2 | 0.2 |
Puting payudara | 0.2 | 0.2 | 0.2 | ||
Kepadatan Massal≥ | Elektrode | G/cm³ | 1.72 | 1.72 | 1.72 |
Puting payudara | 1.80 | 1.80 | 1.80 | ||
(C. T E)≤ | Elektrode | 10-6/ | 1.4 | 1.4 | 1.4 |
Puting payudara | 1.2 | 1.2 | 1.2 |
1.pembungkusan terbagi
Elektrode dan puting dikemas terpisah dan dikirim
2.Pre-connected packing
Puting telah diisi dengan elektrode satu ujung, dan pengiriman dalam kemasan.
Tujuan utama pengemasan:untuk melindungi elektrode dari kerusakan selama penyimpanan dan pengangkutan, terutama dari komponen screw.
Catatan: Kami dapat menyediakan kemasan sesuai dengan kebutuhan pengguna.