Tipe: | bubuk campuran nikel |
---|---|
Standar: | ASTM, GB |
Kelas: | Seri 500 |
Bentuk: | Bundar |
Teknik: | persiapan |
Perlakuan Permukaan: | Dipoles |
Pemasok dengan izin usaha terverifikasi
MIM Antikarat Baja | |||||||||||
Kelas | Komposisi kimia (wt%) | ||||||||||
C | CR | NI | MN | MO | CU | Jml | S | P | Si | O | |
316L | ≤0.03 | 16-18 | 10-14 | ≤2 | 2-3 | - | - | ≤0.03 | ≤0.035 | ≤1 | ≤0.4 |
316 | ≤0.08 | 16-18 | 10-14 | ≤2 | 2-3 | - | - | ≤0.03 | ≤0.035 | ≤1 | ≤0.4 |
304L | ≤0.03 | 18-20 | 8-12 | ≤2 | - | - | - | ≤0.03 | ≤0.035 | ≤1 | ≤0.4 |
304 | ≤0.08 | 16-18 | 8-12 | ≤2 | - | - | - | ≤0.03 | ≤0.045 | ≤1 | ≤0.4 |
17-4PH | ≤0.07 | 15.5-17.5 | 3-5 | ≤1 | - | 3-5 | 0.15-0.45 | ≤0.03 | ≤0.040 | ≤1 | ≤0.4 |
420 | 0.3-0.4 | 12-14 | 0.4-0.6 | ≤1 | ≤0.75 | - | - | ≤0.03 | ≤0.040 | ≤1 | ≤0.4 |
440C | 0.95-1.2 | 16-18 | ≤0.6 | ≤1 | ≤0.75 | - | - | ≤0.03 | ≤0.040 | ≤1 | ≤0.4 |
Distribusi Ukuran partikel (μm) | Kerapatan keran(g/cm3) | ||||||||||
D90 | D50 | D10 | - | ||||||||
GZSL-1 | ≤22.0 | 7.0-8.0 | 2.0-2.5 | 4.6 | |||||||
GZSL-2 | 26.0 | 8.5-9.5 | 2.5-3.0 | 4.7 | |||||||
Hal lain | Kami dapat disesuaikan berdasarkan kebutuhan Anda |
Kelas | MFI (g/10 mnt) | Suhu injeksi (celcius) | Suhu mold () | OSF | Rasio Deinding (%) | Kerapatan Hijau (g/cm3) | Densitas Sintered (g/cm3) |
316L | 800-1500 | 190 | 110 | 1.167 | ≥7.9 | 5.35-5.42 | 7.8 |
304L | 800-1500 | 5.35-5.41 | 7.8 | ||||
17-4PH | 800-1500 | 5.29-5.35 | 7.7 |
Kelas | Sintering | Menghasilkan kekuatan | Kekuatan tensil | Naskh (Naskh) | Kekerasan | Resistan korosi |
316L | ≥7.80 g/cm3 | 184 MPa | 542 MPa | 64% | 80 HRB | 72h |
17-4PH | ≥7.70 g/cm3 | 802 MPa | 854 MPa | 8.5% | 30 HRC | 24h |
Pemasok dengan izin usaha terverifikasi