Refractoriness (℃): | 1580< Refractoriness< 1770 |
---|---|
Feature: | Long Time Materials |
Type: | Refractory Material |
Shape: | Powder |
Material: | Castable |
ukuran butir maks: | 6mm |
Pemasok dengan izin usaha terverifikasi
Cement-Cement Rendah
Item |
GRLC 75 |
GRLC 80 |
GRLC 85 |
GRLC 95 |
Tempescius Servis |
1650 |
1700 |
1750 |
1780 |
Kepadatan Massal (g/cm3) (Dikeringkan pada 110) |
2.55 |
2.6 |
2.7 |
3.0 |
CCS 110 (MPa) 1100celcius 1500 DERAJAT |
65 75 80 |
70 80 85 |
80 90 100 |
90 95 110 |
MATAU 110 (MPa) 1100celcius 1500 DERAJAT |
9 10 11 |
10 11 12 |
11 12 13 |
13 14 15 |
Ukuran butir Maks (mm) |
6 |
6 |
6 |
6 |
Analisis kimia(%)
CAO |
75 2-3 2.4 |
80 2-3 2.0 |
85 2-3 1.8 |
95 2-3 1.5 |
Panduan Aplikasi Mixer Penempatan Air/suhu mixer Waktu Mixing (Min): Kering/basah |
P V 20±5 2/5 |
P V 20±5 2/5 |
P V 20±5 2/5 |
P V 20±5 2/5 |
% Air (biasa) |
7-9 |
7-9 |
6-8 |
6-7 |
Cairable semen rendah didasarkan pada penggunaan kandungan semen kalsium alumina rendah, dan digunakan dalam banyak aplikasi yang memerlukan refraktori tinggi, ketahanan korosi dan resistan abrasi. Struktur ini memiliki struktur yang seragam dengan porositas rendah; memiliki kekuatan suhu tinggi di seluruh rentang suhu rendah dan sedang.
Kandungan CAO semen yang rendah biasanya di bawah 3%, jadi menjamin keadaan stabil berada pada suhu menengah.
Pemasok dengan izin usaha terverifikasi