Type: | Welding Wire Er70s-6 |
---|---|
Material: | Low Carbon Steel |
Flux Containing: | Not Containing Flux |
Slag Characteristic: | Acidic |
Extended Length: | 10-20mm |
oem & odm: | diterima |
Pemasok dengan izin usaha terverifikasi
1 | Nama Produk | KABEL PENGELASAN ( KABEL PENGELASAN MG| KABEL MIGG ) |
ER70S-6 | ||
Pelindung Gas CO2 | ||
Produk pengelasan| Materi Las| Komponen habis dengan pengelasan | ||
2 | Standar Eksekutif | GB/T 8110 ER50-6/ AWS A5,18 ER70S-6/JIS Z3312 YGW12 |
3 | Sertifikat Persetujuan | CCS, ABS, NK, KR, LR, GL, DNV, ISO9001, ISO14001, OHSAS18001 |
4 | Ukuran | 0,8mm, 0,9mm, 1,02mm, 1,2mm, 1,6mm |
5 | Paket | 15kg/D270 spool plastik, 16kg/box, 72kotak/palet, 24palet/1x20'GP |
Bobot bersih: 25,92ton untuk 1x20'GP | ||
Bobot Kotor: 27.80tons untuk 1x20'GP | ||
6 | Ketentuan harga | CIF, CFR, FOB, kesesuaian dengan Aturan INTERMS2010 |
7 | Persyaratan Pembayaran | 30% T/T di muka, keseimbangan 70% terhadap salinan B/L. |
8 | Waktu tunggu | dalam waktu 10 hari setelah menerima deposit |
9 | MOQ | 24 ton untuk satu beban wadah berukuran 20ft |
Komposisi kimia | C | MN | Si | S | P | NI | CR | MO | V | CU |
Jaminan nilai | 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | <=0.025 | <=0.025 | <=0.15 | <=0.15 | <=0.15 | <=0.03 | <=0.50 |
Hasil umum | 0.077 | 1.45 | 0.87 | 0.013 | 0.012 | 0.017 | 0.031 | 0.002 | 0.004 | 0.125 |
Item Uji | RM(N/mm2) | Rel/Rp0,2(N/mm2) | A (%) | V2(J)-40 |
Jaminan nilai | >=500 | >=420 | >=22 | >=47 |
Hasil umum | 555 | 450 | 29 | 77,95,83 |
Nama komoditas | Kelas | AWS | Diameter | Paket | Keterangan |
Kabel pengelasan | ER50-6 | ER70S-6 | 0,8mm | 5/15/20kg/spool, 250/350kg/drum |
MOQ:25MT/1X20'GP |
0,9mm | |||||
1,0mm | |||||
1,2 mm | |||||
1,6 mm | |||||
ER50-G | ER70S-G | 1,0mm | |||
1,2 mm | |||||
1,6 mm |
Standar dan kelas baja | GB | ER49-1 | ER50-3 | ER50-4 | ER50-6 | ER50-G |
AWS | - | ER70S-3 | ER70S-4 | ER70S-6 | ER70S-G | |
Specificationφ(mm) | 0.9-1.6 | 0.8-1.6 | 0.8-1.6 | 0.8-1.6 | 0.8-1.6 | |
Komposisi kimia kabel pengelasan | C | ≤0.11 | 0.06-0.15 | 0.07-0.15 | 0.06-0.15 | ≤0.10 |
MN | 1.8-2.1 | 0.9-1.4 | 1.00-1.50 | 1.40-1.85 | 1.40-1.90 | |
Si | 0.65-0.95 | 0.45-0.75 | 0.65-0.85 | 0.80-1.15 | 0.55-1.10 | |
P | ≤0.030 | ≤0.025 | ≤0.025 | ≤0.025 | ≤0.030 | |
S | ≤0.030 | ≤0.035 | ≤0.035 | ≤0.035 | ≤0.030 | |
CR | ≤0.20 | - | - | - | Al≤0.10 | |
NI | ≤0.30 | - | - | - | Ti0,12-0.20 | |
CU | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.50 | |
Sifat mekanis dari logam terdeposisi | σs(MPa) | ≥372 | ≥420 | ≥420 | ≥420 | ≥420 |
σb(Mpa) | ≥490 | ≥500 | ≥500 | ≥500 | 500-660 | |
σ5(%) | ≥20 | ≥22 | ≥22 | ≥22 | ≥22 | |
AKV J(CELCIUS) | ≥47 | ≥27(-18) | - | ≥27(-29) | ≥47(-20) | |
Shielded gas (gas berpelindung | CO2 | 80Ar+20%CO2 | CO2 | CO2 | CO2 | |
Aplikasi Utama | Untuk pengelasan baja karbon rendah dan beberapa struktur baja campuran rendah | Untuk struktur baja karbon pengelasan dan baja campuran rendah | Untuk pengelasan baja karbon | Untuk pengelasan struktur karbon rendah dan baja berkekuatan tinggi 500MPa | Untuk pengelasan karbon rendah dan struktur baja kekuatan tinggi 500MPa, juga digunakan untuk pengelasan arus tinggi |