Indikator teknis batang inti | |||
TIDAK | ITEM | ECR | FRP |
1 | Kepadatan g/cm³ | 2.1 | 2.1 |
2 | Penyerapan air (±20 2 m, 24 jam) % | <0.03% | <0.03% |
3 | Kekuatan tensil Mpa | >1400 | >1400 |
4 | Kekuatan Melpa | >900 | >900 |
5 | Uji meresapi MIN | >15 | >15 |
6 | Uji Penyebaran Air (1% NaCl merebus 100h,12KV ,1 mnt) μA |
<1000 | <1000 |
7 | Interlaminar Shear Strenrh Mpa | >50 | >50 |
8 | Resistivitas volume(140Ω,96h).m | Tambah penukar ASCII ( PostScript) pada 1.0 1010Ω · | Tambah penukar ASCII ( PostScript) pada 1.0 1010Ω · |
9 | dc:Breakdown Tegangan kv | 150 | 150 |
10 | Waktu voltase penangkal petir (10KV,10mm) |
5 | 5 |
11 | Toleransi permia mm | 0,1 | 0,1 |
12 | Kekuatan tekukan termal (Mpa/150) | >350 | - |
13 | korosi stres h | 96 | - |
14 | Kekuatan torsional Mpa | 70 | 70 |
15 | kandungan serat kaca % | ≤82 | ≤82 |
Tidak | parameter | satuan | spesifikasi |
1 | Kerapatan(pada temperatur 20±2) | g/cm 3 | 2.2 |
2 | Kadar penyerapan air (at20±2 24 jam) | % | 0.05 |
3 | Kekuatan tensil | MPa | 1690 |
4 | Kekuatan Meliuk | MPa | 1100 |
5 | Uji penetrasi kering | Min | 50 |
6 | Tes fussion air (1%nacl,mendidih selama 100h 12kv/1mnt) |
μA | <10 |
7 | Kekuatan pencukuran sepanjang lampal | MPa | 50 |
8 | Resistivitas volume(140,96h) | Ω.M. | 10 10 |
9 | Voltase ketahanan DC (10 menit) | KV | 50 |
10 | Tegangan tahan petir (100kv,10mm) | waktu | 5 |
11 | Kekuatan tekukan pada kondisi pemanasan | MPa/150 | 350 |
12 | Korosi stres (1 mol/1hno3,pada stres 67%) | h | 7200 |
13 | Kekuatan torsi | MPa | 800 |