Application: | Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Insulating Varnish |
---|---|
Type: | Insulation Sheet |
Chemistry: | Hybrid Insulation |
Thermal Rating: | A 105 |
Maximum Voltage: | 20KV~100KV |
Classification: | Inorganic Insulation Material |
Pemasok dengan izin usaha terverifikasi
Kemampuan | Satuan | Contoh | |||||||||||
Target teknik | Sasaran teknik dering | ||||||||||||
P3B | C1B | C2B | C3B | C4B | T2B | T3B | |||||||
Densitas Tampilan | g/cm3 | 1.1-1.2 | 0.7-0.9 | 0.9-1.1 | 1.1-1.2 | 1.2-1.3 | 0.9-1.1 | 1.2-1.3 | |||||
Uap air | % | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | |||||
Kekuatan lekukan arah layer vertikal | Arah A |
MPa | ≥150 | ≥45 | ≥55 | ≥65 | ≥80 | Diameter>1000mm | ≥100 | ≥140 | |||
Arah B |
Diameter≤1000mm | ≥90 | ≥125 | ||||||||||
Arah lapisan vertikal modulus elastisitas | Arah A | IPK | ≥14 | ≥4.5 | ≥6 | ≥8 | ≥9 | ≥10 | ≥13 | ||||
B | |||||||||||||
Tanggung Jawab(di bawah 20MPa) | C | % | ≤3 | ≤5 | ≤4 | ≤3 | ≤2.5 | ≤5 | ≤4 | ||||
CCipta | ≥70 | ≥70 | ≥70 | ≥70 | ≥70 | ≥70 | ≥70 | ||||||
Kekuatan benturan (pengujian samping) |
A | KJ/m2 | ≥35 | ≥6 | ≥10 | ≥13 | ≥15 | ≥25 | ≥35 | ||||
B | |||||||||||||
Kekuatan shear | MPa | ≥8 | ≥5 | ≥7 | ≥8 | ≥9 | ≥7 | ≥9 | |||||
Arah lapisan vertikal Elektrik trkekuatan In (2±90) Oli |
KV/mm | ≥11 | ≥9 | ≥10 | ≥11 | ≥12 | ≥10 | ≥10 | |||||
Arah lapisan paralel Elektrik trkekuatan In (2±90) Oli |
KV | ≥50 | ≥50 | ≥50 | ≥50 | ≥50 | ≥50 | ≥50 | |||||
Srinkage setelah dikeringkan | Arah A | % | ≤0.2 ≤0.5 ≤3 |
≤0.3 ≤0.3 ≤3 |
≤0.3 ≤0.3 ≤3 |
≤0.3 ≤0.3 ≤3 |
≤0.3 ≤0.3 ≤3 |
Ukur | ≤0.5 | ≤0.5 | |||
Arah A | |||||||||||||
≤3 | ≤3 | ||||||||||||
Ketebalan | |||||||||||||
Penyerapan oli | % | ≥8 | ≥20 | ≥15 | ≥8 | ≥5 | ≥10 | ≥5 | |||||
Kontaminasi ke makanan elektrik cair (Δtanδ) |
- | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ||||||