Tipe: | Tanpa sambungan |
---|---|
Teknik: | Dingin |
Material: | Baja Karbon |
Perlakuan Permukaan: | Bright, Black Phosphated, Galvanizing |
Penggunaan: | Pipa Hidraulik/Automobile |
Bentuk bagian: | Bundar |
Pemasok dengan izin usaha terverifikasi
Komposisi Bahan kimia (%) | |||||||||
Standar | Kelas Baja | Nomor Material | C | Si | MN | P | S | CR | MO |
DIN 2391 | ST35 | 1.0308 | <= 0.17 | <= 0.35 | >=0.04 | <=0.025 | <=0.025 | - | - |
ST45 | 1.0408 | <= 0.21 | <= 0.35 | >=0.04 | <=0.025 | <=0.025 | - | - | |
ST52 | 1.058 | <= 0.22 | <= 0.55 | <=1.60 | <=0.025 | <=0.025 | - | - | |
BK | BKW | BKS | GBK | ||||||
Kelas Baja | RM Strtensil ( Mpa) Min | Naskh (Nlonh) (mnt) | RM Strtensil (Mpa) Min | Naskh (Nlonh) (mnt) | RM Strtensil (Mpa) Min | Rel yield Strength(Mpa) Min | Naskh (Nlonh) Min | RM Strtensil (Mpa)Min | Naskh (Nlonh) (%) Min |
ST35 | 480 | 6 | 420 | 10 | 420 | 315 | 14 | 315 | 25 |
ST45 | 580 | 5 | 520 | 8 | 520 | 375 | 12 | 390 | 21 |
ST52 | 640 | 4 | 580 | 7 | 580 | 420 | 10 | 490 | 22 |
Standar | Kelas Baja | Nomor Material | C | Si | MN | P | S | CR | MO |
EN10305-1 EN10305-4 |
E235 | 1.0308 | <= 0.17 | <= 0.35 | >=0.04 | <=0.025 | <=0.025 | - | - |
E255 | 1.0408 | <= 0.21 | <= 0.35 | >=0.04 | <=0.025 | <=0.025 | - | - | |
E355 | 1.058 | <= 0.22 | <= 0.55 | <=1.60 | <=0.025 | <=0.025 | - | - |
Kelas Baja | (+C) | (+LC) | (+SR) | (+A) | (+N) | |||||||
RM Strtensil ( Mpa) Min | Naskh (Nlonh) (mnt) | RM Strtensil (Mpa) Min | Naskh (Nlonh) (mnt) | RM Strtensil (Mpa) Min | Rel yield Strength(Mpa) Min | Naskh (Nlonh) Min | RM Strtensil (Mpa)Min | Naskh (Nlonh) (%) Min | Tenaga tensil RM (Mpa) | Rel yield Strength (Mpa) Min | Naskh (Nlonh) Min | |
E235 | 480 | 6 | 420 | 10 | 420 | 350 | 16 | 315 | 25 | 340-480 | 235 | 25 |
E255 | 580 | 5 | 520 | 8 | 520 | 375 | 12 | 390 | 21 | 440-570 | 255 | 21 |
E355 | 640 | 4 | 580 | 7 | 580 | 450 | 10 | 450 | 22 | 490-630 | 355 | 22 |
Komposisi Bahan kimia (%) | ||||||||||||
Kelas Baja | Nomor Material | C | Si | MN | P | S | CR | MO | Strength RM (Mpa) Min | Menghasilkan kekuatan Reh (Mpa) Min | Naskh (Nlonh) (mnt) | |
ASTM A822-A450 | A822 | - | Maks. 0.18 | - | 0.27-0.63 | Maks. 0.048 | Maks. 0.058 | - | - | 310 | 170 | 35 |
ASTM A179 | A179 | - | 0.06-0.18 | - | 0.27-0.63 | Maks. 0.035 | Maks. 0.035 | - | - | 310 | 170 | 35 |
SAE J524 | J524 | - | Maks. 0.18 | - | 0.3-0.6 | Maks. 0.04 | Maks. 0.05 | - | - | 325 | 180 | 35 |