After-sales Service: | Yes |
---|---|
Warranty: | Yes |
Certification: | CE, ISO, TUV |
Surface: | Textured&Smooth |
Application: | Transportation Project, Hydraulic Project, Geotechnical Project, Environmental Project |
Feature: | Puncture Resistance, Impact Resistance, Tear Resistance |
Pemasok dengan izin usaha terverifikasi
Properti |
Metode Pengujian |
Nilai uji | ||||||||
0.5 mm | 0,75mm | 1.00 mm | 1.25 mm | 1.50 mm | 2.00 mm | 2.50 mm | 3.00 mm | |||
Simpangan maksimal ketebalan | -15% | -15% |
-15% | -15% | -15% | -15% | -15% | -15% | ||
Kepadatan (min ave.) | D 1505/D792 | 0.940 g/cc |
0.940 g/cc |
0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | |
Properti tensil (bagian tengah dari luar) | Menghasilkan kekuatan Kekuatan pecah |
D6693 |
8N/mm | 11 N/mm | 15 N/mm | 18 N/mm | 22 N/mm | 29 N/mm | 37 N/mm | 44 N/mm |
14N/mm | 20N/mm |
27 N/mm | 33 N/mm | 40 N/mm | 53N/mm | 67 N/mm | 80 N/mm | |||
Keuntungan | 12% | 12% | 12% | 12% | 12% | 12% | 12% | 12% | ||
Pengeluaran istirahat | 700% | 700% | 700% | 700% | 700% | 700% | 700% | 700% | ||
Resistansi robek (min ave.) | D 1004 | 63 N. | 93 N. | 125 N. | 156 N. | 187 N. | 249 N. | 311 N. | 374 N. | |
Resistansi kebocoran (min. ave.) | D 4833 | 160N | 240N | 320 N. | 400 N. | 480 N. | 640 N. | 800 N. | 960 N. | |
Konten Hitam Karbon (rentang) | D 4218 | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | |
Waktu Induksi oksidatif (OIT) (min. Kebanyakan) Standar OIT |
D 3895 | 100 mnt | 100 mnt |
100 mnt | 100 mnt | 100 mnt | 100 mnt | 100 mnt | 100 mnt | |
Usia oven pada suhu 85 derajat C Standar OIT (min ave.) - % dipertahankan setelah 90 hari |
D 5721 D 3895 |
55% |
55% |
55% |
55% |
55% |
55% |
55% |
55% |
|
Resistansi UV Tekanan Tinggi OIT (min. ave.) - % dipertahankan setelah 1600 jam |
D 3895 D 5885 |
50% |
50% |
50% |
50% |
50% |
50% |
50% |
50% |
Properti Tes | Satuan | Standar | Frekuensi uji | GM10 | GM15 | GM20 | GM25 |
Ketebalan | mm | D5994 | per rol | 1.00 | 1.50 | 2.00 | 2.50 |
Tinggi Susunan | mm | D7446 | Setiap roll ke-2 (2) | 0.25 | |||
Kerapatan | g/cc | D1505/D792 | 90.000 kg | 0.94 | |||
Properti tensil | |||||||
Menghasilkan kekuatan | KN/m | D6693 Tipe IV |
9,000 kg | 15 | 22 | 29 | 37 |
Kekuatan pecah | KN/m | 10 | 16 | 21 | 26 | ||
Menghasilkan | % | 12 | 12 | 12 | 12 | ||
Naskh (memutus) | % | 100 | 100 | 100 | 100 | ||
Tahan robek | N | D1004 | 20,000kg | 125 | 187 | 249 | 311 |
Resistan kebocoran kebocoran | N | D4883 | 20,000kg | 267 | 400 | 534 | 667 |
Resistansi terhadap retakan tegangan | hr | D5397(Aplikasi) | Per GRI GM-10 | 300 jam | |||
Konten karbon hitam | % | D4218 | 9,000kg | 2.0-3.0% | |||
Dispersi hitam karbon | / | D5596 | 20,000kg | Untuk 10 tampilan berbeda: 9 di Kategori 1 atau 2 dan 1 di Kategori 3 | |||
Waktu Orientasi Oksidatif | |||||||
Standar OIT | min | D3895 | 90.000 kg | 100 mnt | |||
Tekanan tinggi ONIT | / | D5885 | 90.000 kg | 400 mnt | |||
Usia oven pada 85 derajat C dipertahankan setelah 90 hari | % | D5721 | per setiap formula | 55% | |||
Standar OIT | / | D3895 | 80% | ||||
Tekanan tinggi ONIT | / | D5885 | 80% | ||||
Resistansi UV | |||||||
Tekanan Tinggi OIT - % dipertahankan setelah 1600 jam | % | D5885 | per setiap formula | 50% | |||
Lebar Rol | m | / | / | 7 | 7 | 7 | 7 |
Panjang Rol | m | / | / | 210 | 140 | 105 | 70 |
Stabilitas ukuran | % | / | / | 2% |