1030g, Nyon6 30%Serat Kaca,

• Tipe Fiibreboard Glass: Glass Fiber
• Sertifikasi: RoHS
• Teknik: Compound
• warna: alami
• Paket Transportasi: Vacuum Packing Bag
• Spesifikasi: 25kg
• Tidak. Model.: 1030G
• Merek Dagang: moresu
• Asal: China
• Kode HS: 390810
• Kapasitas Produksi: 50000 Tons/Year

Deskripsi Produk

Item	Test condition	Test standards	unit	Typicalvalue
Desity	23ºC	ISO 1183	g/m³	1.36
Molding shrinkage	flow	ISO 294-4	%	0.35-0.7
Melt Flow Rate	23ºC/ 50% r.h.	ISO 1133	g/10min	6.5
Tensile Strength at break	50 mm/min	ISO 527-2	Mpa	150
Elongation at break	5 mm/min	ISO 527-2	%	4
Cantilever notched impact strength	23ºC	ISO 180	kJ/m²	16
Flexural Strength	23ºC	ISO 178	Mpa	190
Flexural Modulus	23ºC	ISO 178	Mpa	7200
Melting temperature	DSC, 10ºC/min	ISO 11357-1	ºC	220
Temperature of deflection	1.80 Mpa	ISO 75-1,-2	ºC	210
Fire Resistance	1.6mm	UL94	Class	HB
GWIT	3.0mm	IEC 60695	ºC	750
GWFI	3.0mm	IEC 60695	ºC	960
CTI	Solution A	IEC 60112	V	250
Pre-drying temperature			ºC	90~110
Pre-drying time			h	3~4
Injection temperature			ºC	250~280
Mold temperature			ºC	80~100

Advantages of glass fiber reinforced nylon:

1.Adding 30% glass fiber to nylon significantly improves its mechanical properties, dimensional stability, heat resistance, and aging resistance, with a fatigue strength 2.5 times that of unreinforced nylon.

2. Due to the addition of glass fiber, it can limit the mutual movement of polymer chains in plastic, resulting in a significant decrease in its shrinkage rate. The shrinkage phenomenon of plastic products is much better than before the addition of glass fiber, and the rigidity is also improved Improved a lot.

3. Glass fiber reinforced nylon has high mechanical strength, wear resistance, self-lubrication, good electrical insulation, self extinguishing, non-toxic, odorless, and good weather resistance.

4. After being reinforced with fibers, nylon can reduce the water absorption of nylon chips, enabling them to work in high-temperature and high-temperature environments.